Enhanced room-temperature NH 3 sensing properties of Cu 2 O concave octahedron/CNTs heterostructured hybrid via efficient charge transfer
Kun Zhao,Jiahong Tang,Shouqin Tian,Xiang Li,Huimin Yang,Xiaoxia Wang,Dawen Zeng
DOI: https://doi.org/10.1016/j.snb.2023.133724
2023-03-25
Abstract:As a typical semiconductor metal oxide, Cu 2 O concave octahedrons exposed with high-energy facets have attracted much attention due to their good gas-sensing performance, but their gas sensors usually exhibit very large baseline resistance at room temperature which usually exceed the testing limitation and thus cannot be applied widely. Herein, Cu 2 O concave octahedrons exposed with high-energy facets (511) were hybridized with carbon nanotubes (CNTs) to form Cu 2 O/CNTs heterostructures and then employed as gas sensors. The sensor exhibited lower baseline resistance and higher response to NH 3 gas at room temperature compared with that pure Cu 2 O. This was probably because that efficient charge transfer between exposed {511} facets of Cu 2 O concave octahedrons and CNTs can reduce the baseline resistance greatly, and also facilitate the adsorption of more oxygen and subsequent reaction with NH 3 gas, leading to an increased response. In addition, sensor response was increased at first and reached the maximum at 5%, and then decreased with increasing the content of CNTs from 1% to 10%. This was probably because excess CNTs can reduce adsorption sites of Cu 2 O particles and thus result in a low response. Therefore, this work can provide a facile method to fabricate room-temperature NH 3 sensor with high performance.
chemistry, analytical,electrochemistry,instruments & instrumentation