Abstract:The characteristics of electrical treeing in ice-water quenched high-density polyethylene (HDPE) film under AC voltage of different frequency ranging from 50 Hz to 90 kHz was studied. The electrical treeing experiments are carried out at room-temperature. The processes of electrical treeing during the experiment are observed via a digital micro-observing system. It was found that under different frequency of applied voltage the initiation shape of electrical tree was different, it means the different mechanisms of electrical tree initiation. There are 4 kinds of trees in inception period: branch tree, trunk tree, bush tree and breakdown tree. Trunk tree and breakdown tree with high initiation speeds are special kinds appearing in high frequency (HF). The branch tree is the primary shape in the range of low frequency, while the bush tree is the primary shape in the range of HF. With the increase of frequency, the occurrence ratio of branch tree decreases, while the occurrence ratio of bush tree increases. It was also shown that as the propagation of electrical tree, the conversion of tree shape is strongly affected by the frequency. The electrical tree usually has a simple shape and rarely changes under low frequency in one hour or more. However, in the case of a higher frequency, the electrical tree shape changes more frequently and has a large probability to breakdown. The result also showed that there were 4 steps in the electrical tree propagating process: initiation step, stagnation step, growth step and breakdown step. Under the same voltage, high frequency could accelerate the electrical tree propagation. Higher frequency could speed up the tree growing and increase the probability of breakdown caused by electrical tree. The influence of frequency on material polarization process, fatigue and thermo effect were considered as the main causes of the experiment results. The more serious destruction caused by high frequency electrical treeing degradation can well explain the reason of insulation premature inactivation in mid-frequency or high-frequency electrical equipment.

Effect of Frequency on Electrical Treeing Characteristicsof High-density Polyethylene

Influence of Frequency on Electrical Tree Initiation in Polyethylene

Breakdown Phenomena Caused by Electrical Tree Degradation in High Density Polyethylene under High Frequency Voltage

Propagation and Partial Discharge Characteristics of Electrical Trees in 110 Kv XLPE Cable Insulation at Power Frequency Applied Voltage

Influence of Frequency on Electrical Tree Initiation in High-Density Polyethylene

The Effect of DC Electro-thermal Ageing on Electrical Treeing in Polyethylene

The Initiation and Propagation of Electrical Trees at Different Electric Field and Temperature in XLPE

Treeing Phenomenon In Polyethylene Under High Frequency Voltage

Trees in 110 kV XLPE cable insulation at high temperature

Electrical Treeing Behavior of DC and Thermally Aged Polyethylenes Utilizing Wire-Plane Electrode Geometries

Partial Discharge and Growth Characteristics of Electrical Trees in 110kV XLPE Cable Insulation at High Temperature

Electrical treeing behavior at high temperature in XLPE cable insulation samples

Three-Dimensional Nanometer Features of Direct Current Electrical Trees in Low-Density Polyethylene.

Electrical tree formation as a measure of degradation resistance in polymeric materials for HVDC applications

Investigation of temperature effect on electrical trees in XLPE cable insulation

AC and DC Pre-Stressed Electrical Trees in LDPE and Its Aluminum Oxide Nanocomposites

Study on conducting characteristics of electrical trees in cross-linked polyethylene cable insulation

The Electrical Trees Initiation at Different Electric Field Strength in XLPE Cable Insulation

On the Conducting and Non-Conducting Electrical Trees in XLPE Cable Insulation Specimens

Electrical Treeing in Polyethylene-Alumina-filled Nanocomposites for HVDC Applications