Abstract:Nd2Fe14B hard magnetic nanoparticles were synthesized by chemical synthesis techniques. Nd-Fe-B gel was prepared using NdCl3 center dot 6H(2)O, FeCl3 center dot 6H(2)O, H3BO3, citric acid, and ethylene glycol (EG) by a Pechini type sol gel method. This gel was subsequently annealed to produce mixed oxide powders. Nd2Fe14B nanoparticles were prepared from these oxides by a reduction diffusion process. The phase analysis, structure, and magnetic properties were determined by Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance (NM R), X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), transmission electron microscope (TEM), and vibrating sample magnetometer (VSM) techniques. The mechanism of Nd2Fe14B formation was investigated by differential scanning calorimetry (DSC), XRD, and thermodynamic free energy change data. Our experimental and modeling results showed that the reduction diffusion of the Nd-Fe-B mixed oxide was a three step process. The reduction of Fe2O3 to Fe and B2O3 to B occurred at 300 degrees C. NdH2 and Fe was formed from Nd2O3 and NdFeO3 at 620 degrees C. The Nd2Fe14B phase was formed from NdH2, Fe, and B at 692 degrees C. The coercivity of as-synthesized powder was 6.1 kOe. The Henkel plot showed that this powder was exchange coupled; removal of CaO by washing led to dipolar interactions and a decrease in coercivity.

Sol-gel Synthesis of the Soft Magnetic Compound Oxide of Cobalt and Neodymium and Its Characterization

Structural Analysis for Preparing Substituted Sr Hexaferrite Nanoparticles by Sol-gel Method

Preparation and Characterization of Cesium and Cobalt Complex Oxide

Formation of sol-gel in situ derived BTO/NZFO composite ceramics with considerable dielectric and magnetic properties

Bulk Alpha-Fe/Nd2fe14b Nanocomposite Magnets Prepared by the Phase Transition of Amorphous Nd9fe81co3nb1b6 under High Pressure

Sol-hydrothermal synthesis and characterization of nano strontium cobalt oxide.

Study of Preparation of Cobalt Aluminate by Sol-Gel Process and Electroless Plating

Bulk Mg-doped Spherical Lithium Cobalt Oxide Preparation and Characterization of Precursor

Study of preparation of cobalt cerium complex oxides catalyst by sol-gel method

Preparation of Nanocrystalline Composite Permanent Magnet Mterials and Exchange Coupled Effect

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Nd2Fe14B hard magnetic powders: Chemical synthesis and mechanism of coercivity

Effect of Gd and Co Contents on the Microstructural, Magneto-Optical and Electrical Characteristics of Cobalt Ferrite (cofe2o4) Nanoparticles

Hydrothermal Synthesis and Optical, Magnetic, and Supercapacitance Properties of Nanoporous Cobalt Oxide Nanorods

Synthesis of Cobalt Ferrite Nanoparticles and Effect of Doped Lanthanum on Magnetic Properties of Cobalt Ferrite

Bulk anisotropic nanocomposite magnets prepared by the thermo-mechanical processing of Nd3.6Pr5.4Fe83Co 3B5 with different microstructures

Alteration of magnetic behavior of (Mg0.9Ni0.1O)x/(CoFe2O4)1-x nanocomposites

Sol–gel Synthesis, Magnetic and Magneto-Optical Properties of CoFe2−xTbxO4 Nanocrystalline Films

Sol−Gel Based Chemical Synthesis of Nd2Fe14B Hard Magnetic Nanoparticles

Enhanced Magnetoresi Stance In La0.7sr0.3mno3/Nd0.7sr0.3mno3 Nanocomposites

Electronic Structure of NdFeCoB Oxide Magnetic Particles Studied by DFT Calculations and XPS