Abstract:Polyacrylonitrile (PAN) precursor nanofibers are prepared by traditional electrospinning and the centrifugal spinning, respectively. The nanofiber bundles are drawn in hot air with a constant force into 1 and 3 times of the original length. Subsequently, the crystalline structure, orientation, morphology, diameter of PAN nanofibers before and after drawing treatment were characterized by WAXD and SEM. The results show that: (1) the efficiency of centrifugal-electrospinning is far higher (120 times) than that of electrospinning (fluid flow rate of centrifugal-electrospinning: 2 mL/min, fluid flow rate of electrospinning: 1 mL/h). (2) Despite a low crystallinity from centrifugal spinning or electrospinning (the crystallinity of the PAN nanofiber precursor by centrifugal spinning is 25%, while that by electrospinning is 10.6%). PAN precursor nanofibers prepared by centrifugal spinning have certain orientation (60.5%); while those prepared by electrospinning have almost no orientation; (3) Hot-air-drawing with a constant force (1.00 N) contributes to a higher crystallinity (centrifugal spinning: 45.8%, electrospinning: 36.2%) and orientation (centrifugal spinning: 72.5%, electrospinning: 59.8%) for the PAN nanofibers. Moreover, increased drawing temperature and force results in a decrease in the diameter of the PAN nanofiber bundles (the diameter of PAN nanofibers prepared by centrifugal spinning decreases from 675 nm to 510 nm; while that by electrospinning decreases from 460 nm to 355 nm). Compared with the slight effect of the spinning process on crystalline structure and orientation, the hot-air drawing treatment significantly promotes the crystalline and orientation. The centrifugal force is helpful to eliminate the whip phenomenon and to make a full drawing of jet flow, finally leading to a higher certain orientation for the polymer chains of PAN nanofibers.

Vibrorheological Effect on Electrospun Polyacrylonitrile (pan) Nanofibers

Fabrication of Nanofibers by Low-Voltage Near-Field Electrospinning

Polymer Nanofibers Prepared by Low-Voltage Near-Field Electrospinning

Highly-efficient Fabrication and Crystallinity and Orientation of Polyacrylonitrile Nanofibers

Preparation and Properties of Poly (vinyl Alcohol) Nanofibers by Electrospinning

Morphological Modulation of Electrospun PVDF/PVP Nanofibers

Polyacrylonitrile and Carbon Nanofibers with Controllable Nanoporous Structures by Electrospinning

Tailoring the Morphologies of Pvdf Nanofibers by Interfacial Diffusion During Coaxial Electrospinning

Fabrication of Poly(vinylidenefluoride‐co‐hexafluoropropylene) Nanofiber Yarns by Conjugate Electrospinning

Preparation and characterization of pan nanofiber via electrostatic spinning

Investigation of Post-Spinning Stretching Process on Morphological, Structural, and Mechanical Properties of Electrospun Polyacrylonitrile Copolymer Nanofibers

Enhanced Mechanical Performance of Electrospun Graphene/Polyacrylonitrile (PAN) Composite Microfibrous Yarns Via Post-Processing

Effects of Chemical Composition and Post-Spinning Stretching Process on the Morphological, Structural, and Thermo-Chemical Properties of Electrospun Polyacrylonitrile Copolymer Precursor Nanofibers

Influence of Solvents on the Formation of Ultrathin Uniform Poly(Vinyl Pyrrolidone) Nanofibers with Electrospinning

On fabrication of nanoscale non-smooth fibers with high geometric potential and nanoparticle’s non-linear vibration

Hydrogen Bonding-Driven Rheological Modulation of Chemically Reduced Graphene Oxide/poly(vinyl Alcohol) Suspensions and Its Application in Electrospinning.

Effects of Electrospinning Technological Parameters on Diameter of Polyacrylonitrile Insulation Nano-fiber

Preparation of porous hollow polyacrylonitrile ultrafine fibers by coaxial electrospinning

Nanostructured Electrospun Hybrid Graphene/Polyacrylonitrile Yarns

The effects of electrospinning parameters on coaxial polyacrylonitrile/polyurethane nanofibers: Morphology and water vapour transmission rate

Controlling Poly(p-Phenylene Vinylene)/poly(vinyl Pyrrolidone) Composite Nanofibers in Different Morphologies by Electrospinning