Abstract:Water-colloid cadmium selenide semiconductor nanocrystals were prepared in aqueous solution by(using) mercaptoacetic acid as stabilizer.The samples were characterized by X-ray photoelectron spectroscopy(XPS) and transmission electron microscopy(TEM).The results of XPS confirmed the formation of CdSe nanocrystals,and the images of TEM demonstrated that the average size of CdSe nanocrystals was less than 10 nm and the aggregation occurred among the nanocrystals.The changes of the XRD patterns,Absorption spectra and(emission) spectra of the CdSe nanocrystals prepared for different time were investigated.The XRD patterns showed that the crystal structure became more perfect with the increasing preparation time.It was found that the emission peak changed from 550 nm to 572 nm, but no distinct changes for the shape and full width at the half maximum of the spectra were observed,but the Absorption peak changed from 443 nm to 483 nm.The extent of the peak changes became less and less with the reaction time,which was attributed to the growth of the CdSe nanocrystals with the reaction time at the initial moment and the control of the growth due to the stabilizer mercaptoacetic acid at the ultimate moment.The emission spectra for the different molar ratios of the reactant were also investigated,and the results indicated that the wavelength of the emission peak shifted to the longer wavelength as the molar ratio of Se~(2-)/Cd~2~+ increased,and it could be interpreted as followings: In the competition between the reaction of Cd~(2+)with HSe~-and RS~-,the reaction between Cd~(2+) and HSe~-occupied the predominance with the increasing of Se amount,which made the size of the nanocrystals increase.All the(results) indicated that the varying of the preparation conditions would influence on the luminescence properties greatly.

Optimization of Preparation Conditions and Surface Modification of Water-soluble Quantum Dots

Synthesis and Optimization of Water-Soluble CdSe/CdS Nanocrystals

Synthesis And Characterization Of Water-Soluble Cdse/Cds/Zns Core-Shell Quantum Dots

Synthesis and Storage of High-Quality CdSe/ZnS Quantum Dots in an Organic Phase

Preparation and Luminescent Properties of CdSe and Core-Shell CdSe/CdS Quantum Dots in Aqueous Solution

Photoluminescence Properties Of Citrate-Stabilized Water-Soluble Cdse And Cdse/Cds Quantum Dots

Optimized Synthesis of CdSe Quanum Dots via a Cyclohexane-Water Two-Phase Approach

Synthesis And Characterization Of Water-Soluble Cdse/Zns Core-Shell Nanoparticles

Preparation of stable, water-soluble, highly luminescence quantum dots with small hydrodynamic sizes

Synthesis and Characterization of Monodisperse CdSe Quantum Dots in Different Organic Solvents

Preparation and Characterization of High Quality CdSe Quantum Dots in Aqueous Solution

[Study of Water-Sol Core-Shell CdSe/CdS Quantum Dots].

Aqueous Synthesis of CdTe/CdS/ZnS Quantum Dots and Their Optical and Chemical Properties

Characterization of Nucleation and Growth Kinetics of the Formation of Water-Soluble Cdse Quantum Dots by Their Optical Properties

A Greener Synthetic Route to Oleylamine/Oleic Acid Capped CdSe Quantum Dots

Aqueous L-cysteine Capped CdTe and CdTe/CdS Core-Shell Quantum Dots: Preparation and Characterization

Influence of Preparation Conditions of CdSe Nanocrystals on Luminescence Properties

Synthesis of CdSe Quantum Dots (qds) in the Water

Facile Synthesis and Characterization of Highly Fluorescent and Biocompatible N-acetyl-L-cysteine Capped CdTe/CdS/ZnS Core/shell/shell Quantum Dots in Aqueous Phase.

Influence factors for the synthesis of water-soluble CdSe/CdS core-shell nanoparticles and their effects on the spectral characterization of CdSe/CdS

Study on the Luminescence Stability of CdSe/CdxZn1-xS Quantum Dots During the Silication Process