Abstract:CdS nanorods of high aspect ratio were synthesized through the route of chemical bath deposition under a mild condition. Diphenylthiocarbazone (DPTA) was employed as an organic additive for the synthesis of CdS nanorods. The crystalline and microstructure of CdS nanorods were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns indicate the existence of both cubic and hexagonal phases in the samples. The sample with the pH value of 10.5 showed a hexagonal (111) peak of maximum intensity, indicating the preferential orientation along the c axis of hexagonal CdS phase. Meanwhile, the cubic phase appeared at the pH value of 10.5. The TEM images reveal that the morphology of CdS could be controlled by adjusting the pH value. Highly crystalline CdS nanorods with the diameter of about 50 nm and the length of about 3 mu m were obtained at the pH value of 10.5. The effects of the pH value on the formation of CdS nanorods were studied. The electrical properties of the samples were also investigated. The results show that the sample prepared with DPTA as the organic additive exhibited a much lower resistance than those prepared with PVA as the additive and in pure ethanol. There were two big pi bonds in a DPTA molecule, which benefited the electron transfer. Finally, the growth mechanism of CdS nanorods and electron transfer in DPTA modified CdS nanorods were discussed.

Preparation and Characterization of Water-Soluble CdS Nanocrystals by Surface Modification of Ethylene Diamine

Synthesis and Characterization of MCCs Capped Water Soluble CdSe QDs

Preparation of CdS Nanoparticles by Hydrothermal Method in Microemulsion

Synthesis And Characterization Of Water-Soluble Cdse/Zns Core-Shell Nanoparticles

Synthesis And Characterization Of Water-Soluble Cdse/Cds/Zns Core-Shell Quantum Dots

Effect of Solvents on Morphology and Size of CdS Nanoparticles via a Solvothermal Route

Ph-Dependent Shape Changes of Water-Soluble CdS Nanoparticles

Synthesis of CdS nanoparticles in water/DMF medium: an investigation on the effect of time and microwave irradiation

Synthesis and Characterization of CdSe Nanoparticles from Aqueous Solution of Selenosulfate

CHARACTERISTICS OF CdS NANOPARTICLES SYNTHESIZED BY SOLVOTHERMAL ROUTE WITH DIFFERENT RATIOS OF ETHYLENEDIAMINE/WATER

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Photoluminescence Properties Of Citrate-Stabilized Water-Soluble Cdse And Cdse/Cds Quantum Dots

Preparation and Growth Mechanism of CdS Nanorods via Chemical Bath Deposition

Effect of solvents on morphology and size of US nanoparticles via a solvothermal route

Phase Transition of CdS in the Presence of Ethylenediamine and Formation of Hollow CdS Submicron Particles with Needle-Like Structure

Synthesis and Photocatalytic Performance of Dendritic CdS Nanostructures by an Ionic Liquid-assisted Hydrothermal Route

Water-Soluble Cdse and Cdse/Cds Nanocrystals: A Greener Synthetic Route

Synthesis and Optical Properties of Nanosized CdS Prepared in a Quaternary CTAB/n-hexanol/n-heptane/water Reverse Micelle

Preparation of water-soluble CdTe/CdS core/shell quantum dots with enhanced photostability

Solvothermal synthesis of nanocrystalline cadmium sulfide