Mineralogical Mechanochemical Agent Assisted Reconditioning Effects and Mechanism on Worn Ferrous Surfaces

Jin Yuansheng,Yang Zhongxue

DOI: https://doi.org/10.1007/978-3-642-03653-8_149

2009-01-01

Abstract:A mineralogical mechanochemical reconditioning agent as a new member of the triboadditive family together with the traditional ones (friction modifiers, antiwear and extreme pressure additives) has been developed in light of the mechno-chemical reaction principle. Its reconditioning effects and mechanism on worn ferrous surfaces were investigated in detail in this paper. The agent package is formulated from a fine-powdery multi-component mixture of Serpentine minerals. The main reconditioning component is magnesium silicate hydroxide (Mg-6(Si4O10)(OH)(8)), with the surfactants for dispersing the main component into bulk lubricant and the catalysts for facilitating interfacial mechanochemical reactions. With commercial fully formulated engine oils as benchmark, the reconditioning effects of the agent package have been demonstrated both in laboratory tribotest and in the field trial for locomotive diesel engine. Surface examination of sampled worn surfaces on both laboratory test specimens and cylinder bore of locomotive diesel engine has shown that a nanocrystalline reconditioning layer ha S been generated which possesses nanometric roughness, higher surface hardness and proper H/E ratio. Advanced analyses have indicated that the inorganic species (ferrite and Fe-C matrix) construct the skeleton structure of the layer with some organic species (hydrocarbon and its ramification) and simpler inorganic species (Fe3O4 and FeOOH nanoparticles, as well as graphite and DLC) adhering on or dispersing in the bulk structure, offering the whole effectiveness of tribological defense of the reconditioning layer, i.e., friction reduction, wear abatement, extreme-pressure and reconditioning worn surface. Analysis of used oils in the field trial and crankcase simulation experiment in laboratory have suggested that generation mechanism of the reconditioning layer involves three interwoven processes: oxidative mechanical polishing, carbonization and graphitization of micro-lubricant on the contact regions, and mechanical alloying.