Synthesis of 2,6-Diisopropylaniline by Gas-Phase Amination on Mg-Al Spinel-Supported Pd-La Catalyst
RX Jiang,ZK Xie,CF Zhang,QL Chen
DOI: https://doi.org/10.3321/j.issn:0253-9837.2003.07.004
IF: 16.5
2003-01-01
Chinese Journal of Catalysis
Abstract:2,6-diisopropylaniline (2,6-DIPA) is an important intermediate in organic chemical industry. The methods to synthesize 2,6-DIPA have been developed in two different ways, alkylation of aniline and gas-phase amination of 2,6-diisopropylphenol (2,6-DIPP). The gas-phase amination is an ideal method for the synthesis of 2,6-DIPA for its high conversion and selectivity, but the reaction condition (such as space velocity) and catalyst stability still need to be improved. In this paper, the magnesia-alumina spinet support was prepared by impregnating Al2O3 with an aqueous solution of aluminium nitrate and magnesium nitrate and then calcinating at high temperature. The Pd-La/spinel catalyst was obtained by impregnating the spinet support with an aqueous solution of palladium chloride and lanthanum nitrate and used in the gas-phase amination of 2,6-DIPP at a high liquid hourly space velocity of 0.3 h(-1) for a relative long time of 300 h. The conversion of 2,6-DIPP, selectivity for 2,6-DIPA, and yield of 2,6-DIPA dropped from 98.5%, 88.9%, and 87.5% to 61.8%, 69.3%, and 42.8%, respectively, after reaction for 480 h. The fresh and coked catalysts were characterized by BET surface area I XRD, TGA, and SEM measurements. The results showed that the two kinds of coke formed on the metal and the support could be burnt up at about 242 and 324 degreesC, respectively. The coke contains aromatic and aliphatic rings, alkyl groups, condensed ring aromatic hydrocarbon, and amine groups. The reason for catalyst deactivation can be explained as follows: both the product 2,6-DIPA and the intermediate product 2, 6-diisopropylcyclohexamine are large basic molecules, they can adsorb on the acid catalyst support easily and generate larger molecules that form carbon deposit on the catalyst through polymerization. The basic promoter La can neutralize the strong acid sites on the catalyst and inhibit the formation of carbon deposit.