Optimization of microstructure and multiferroic properties of BFO–BTO/BaM composites through cold sintering and post-annealing
Zilong Yu,Juan Liu,Yu Sun,Tulai Sun,Mengru Ge,Lihong Bai,Ailin Xia
DOI: https://doi.org/10.1007/s10854-024-13846-0
2024-11-23
Journal of Materials Science Materials in Electronics
Abstract:Conventional sintering method was usually used to prepare composite multiferroic materials, which may lead to some problems, such as uneven grains and large leakage current. In the present work, cold sintering method was applied to overcome these problems. BiFeO 3 –BaTiO 3 /BaFe 12 O 19 (BFO–BTO/BaM) composites were prepared using a cold sintering process and subsequently densified through annealing treatment. The density and the grain size of the composites increased with increasing annealing temperature, and the cold-sintered samples exhibited more uniform grain sizes compared to those produced by normal sintering, indicating that the cold sintering process promotes the densification of ceramics and facilitates the production of grain-uniform ceramics. The study of cold sintering process indicates that at relatively low annealing temperatures, increasing the pressure holding time is beneficial for optimizing performance. However, when the annealing temperature is sufficiently high, the pressure holding time has less impact on performance. The leakage current density decreased significantly when the annealing temperature exceeded 850 °C, and the breakdown electric filed was enhanced in cold sintering assisted samples, which can be attributed to a reduction in space charges. The ferroelectric properties were optimized, achieving a remanent polarization ( P r ) as high as 24.4 μC/cm 2 , which indicating that cold sintering method enhanced the ferroelectric properties of composites. Additionally, the magnetic properties were improved in cold sintering samples.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied