Preparation and Characterization of Co/Co<SUB>9</SUB>S<SUB>8</SUB>/ZnO Core-shell Nanoshperes: Preparation and Characterization of Co/Co<SUB>9</SUB>S<SUB>8</SUB>/ZnO Core-shell Nanoshperes
Wen-Zhong LAI,Xiao-Jie DONG,Jing HUANG,Yong-Hua LENG,Xing-Guo LI
DOI: https://doi.org/10.3724/SP.J.1077.2010.00265
IF: 1.292
2010-01-01
Journal of Inorganic Materials
Abstract:Co/Co9S8/ZnO core-shell nanoshperes were successfully prepared via a thermal decomposition in the water and oxygen-free environmert. The lattice-match between Co9S8 and ZnO played a significant role on the layer-by-layer self-assembly of the core-shell nanospheres. The as-synthesized nanospheres were characterized by XRD, TEM, SQUID and Photoluminescence Spectra. By controlling the reaction parameters, the core-shell nanostructure with uniform size of about 60 nm and shell thickness of 13.6nm was obtained. The effects on the shape control of the product were further investigated, and a proper formation mechanism of the Co/Co9S8/ZnO core-shell nanostructures was presumed. The results show that the favorable procedure to obtain the core-shell nanostructure shape is as follows, the reactants of OLA as solution and TOPO as surfactant, and the optimal temperature and quantity for precursor Zn(acac)(2) is 70 degrees C and 1 mmol, respectively, in additon, the sulfidation reaction time for Co is 5 min. The products show ferromagnetism at room temperature with a coercive force of 18.7kA/m. In the photoluminescence measurement, the strongest peak at 460nm which is attributed to oxygen defects can be obtained, while the band edge transitions of ZnO between 380nm and 390nm can hardly be observed.