Fluorine Doping of Spherical Spinel Limn2o4

XM He,JJ Li,Y Cai,YW Wang,HR Ying,CY Jiang,CR Wan

DOI: https://doi.org/10.1016/j.ssi.2005.07.012

IF: 3.699

2005-01-01

Solid State Ionics

Abstract:Fluorine-doped spherical spinel LiMn2O4 was prepared by controlled crystallization from cheap carbonates. The fluorine bulk and surface doping of spherical samples showed different effects at the same doping amount. 5% fluorine surface-doped sample with Li/Mn=1.15/2 presented both good cycleability and high tap density of 2.1 g cm−3. Its initial specific capacities were 111 and 104 mA h g−1 at 25 and at 55 °C, respectively. Its capacity retentions reached 98.2% and 87.5% at 25 and at 55 °C, respectively, at 50th cycle. There was small difference between the capacity at 25 and 55 °C during cycling. This is of practical value to the enhancement of overall performance of LiMn2O4 both at room temperature and at elevated temperature.