Controllable phase transformation of fluoridated calcium phosphate ultrathin coatings for biomedical applications
Xiang Ge,Jianming Zhao,Xiong Lu,Zhaoyang Li,Kefeng Wang,Fuzeng Ren,Menghao Wang,Qun Wang,Bao Qian
DOI: https://doi.org/10.1016/j.jallcom.2020.155920
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>Titanium has been widely used in medical implants for hard tissue replacements. Nevertheless, the bioinert innate oxide layer on the titanium implant surface usually makes the implant fail to osseointegrate with the surrounding tissue after surgery. To improve the bioactivity of titanium implants, the deposition of calcium phosphate (CaP) coatings attracts much research interest owing to the excellent bioactivity and biocompatibility of CaP. This work successfully developed a promising synthetic method to prepare uniform fluoridated CaP coatings with ultrathin thicknesses (∼170 nm) and desired phases on acid etched pure titanium (AETi) substrates. A dense ultrathin coating with a dominant phase of fluoridated amorphous CaP (FACP) was obtained by an electrochemical deposition method in galvanostatic mode. After a heat treatment at 600 °C for 3 h in a humid atmosphere, the as-prepared coating was transformed to a coating with a dominant phase of fluoridated hydroxyapatite (FHA). Additionally, the dominant phase of the coating could be transformed from FACP to α-tricalcium phosphate (α-TCP) by a heat treatment at 800 °C for 3 h. Unlike previously reported fluoridated CaP coatings with thicknesses of around several micrometers, the ultrathin thickness could potentially enhance the adhesive strength and ductility of coating. Notably, the fluorine incorporation in the coating could bring in additional benefits such as lower solubility, higher antibacterial activity, and higher adhesive strength. Electrochemical deposition associated with post heat treatment could obtain fluoridated CaP coatings with different desired phases in a controllable manner, which is very important since CaPs with different phases possess different properties and may be suitable for different biomedical applications. This study proposed a promising, simple, and low-cost method which can endow complex-shaped titanium implants with better bioactivity for dental and orthopedic applications.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering