Abstract:This work explores the application of biomimetic micro-texturing on the Grey Cast Iron (GCI) surface to reduce frictional wear and thermal fatigue in applications of automotive drum brakes, particularly in heavy vehicles. This study aims to improve the mechanical properties of cast iron specimens using laser surface texturing with tungsten deposition. The outcomes were evaluated using characterization methods, such as scanning electron microscopy, electron dispersive spectroscopy and X-ray diffraction analysis. The microhardness and surface roughness were measured using a microhardness and surface roughness tester. The wear tests were carried out on the pin-on-disc wear testing machine with loads of 4 kg for 7 min of trials. The improvement in surface hardness and roughness of GCI samples resulted in wear mitigation due to frictional forces. Further, in a wear study, Spheroidal Graphite (SG.) Cast Iron is used in hot rolling roll applications. Laser-cladded samples with tungsten deposition showed reduced wear mitigation with a reduction in friction force of 8.53% compared to untreated SG iron samples. These laboratory test measurements and outcomes proved that this method should be further validated for actual rolling conditions. Similarly, the next step in practical field trials is implementing this surface modification technique in actual automotive drum brakes. This study suggests that the methodology could be translated from lab scale to surface engineering applications in cast iron automotive components to improve hardness and wear resistance. Biomimetic material texturing using lasers opens up possibilities for applications such as repairing components like crankshafts and piston rings and mitigating crack propagation in GCI brakes and SG Iron hot rolling rolls.

Thermal Fatigue Behavior of Gray Cast Iron with Striated Biomimetic Non-Smooth Surface

The thermal fatigue resistance of cast iron with biomimetic non-smooth surface processed by laser with different parameters

Effects of Surface Shape on Thermal Fatigue Resistance of Biomimetic Non-Smooth Cast Iron

Effects of C content on the thermal fatigue resistance of cast iron with biomimetic non-smooth surface

Study on Preheating and Annealing Treatments to Biomimetic Non-Smooth Cast Iron Sample with High Thermal Fatigue Resistance

Thermal Fatigue Characteristics of Gray Cast Iron with Non-Smooth Surface Treated by Laser Alloying of Cr Powder

Frictional Wear and Thermal Fatigue Behaviours of Biomimetic Coupling Materials for Brake Drums

Effects of Graphite Shape on Thermal Fatigue Resistance of Cast Iron with Biomimetic Non-Smooth Surface

Effects of pre-placed coating thickness on thermal fatigue resistance of cast iron with biomimetic non-smooth surface treated by laser alloying

Thermal fatigue behavior of 3Cr2W8V die steel with biomimetic non-smooth surface

Investigation of Nanomechanical Properties and Thermal Fatigue Resistance of Gray Cast Iron Processed by Laser Alloying

Different Thermal Fatigue Behaviors Between Gray Cast Iron and Vermicular Graphite Cast Iron

Biomimetic Coupling Effect of Non-Smooth Mechanical Property and Microstructural Features on Thermal Fatigue Behavior of Medium Carbon Steel

Study on Microstructure and Properties of Laser Melting Unit of HT200

The Comparative Study of Thermal Fatigue Behavior of H13 Die Steel with Biomimetic Non-Smooth Surface Processed by Laser Surface Melting and Laser Cladding

Effects of Different Graphite Types on the Thermal Fatigue Behavior of Bionic Laser-Processed Gray Cast Iron

Effect of Thermal Fatigue Loading on Tensile Behavior of H13 Die Steel with Biomimetic Surface

Biomimetic approach in surface modification for improvement in the mechanical properties of implements

Influences of Single Laser Tracks' Space on the Rolling Fatigue Contact of Gray Cast Iron

Thermal Cycling Effect on the Wear Resistance of Bionic Laser Processed Gray Iron

Bio-inspired Wearable Characteristic Surface: Wear Behavior of Cast Iron with Biomimetic Units Processed by Laser