ELECTROCHEMICAL BEHAVIOR OF Fe-20Cr NANOCRYSTALLINE COATINGS

MENG Guozhe,LI Ying,WANG Fuhui

DOI: https://doi.org/10.3969/j.issn.1005-4537.2006.01.003

2009-01-01

Abstract:Fe-20Cr nanocrystallized coatings(NC) were prepared by magnetron sputtering on a glass substrate.The potentiodynamic polarization of Fe-20Cr cast alloy and NC were measured respectively in 0.05 mol/L H_2SO_4+0.25 mol/L Na_2SO_4 and 0.05 mol/L H_2SO_4+0.5 mol/L NaCl solutions.The results showed that NC has greater trend to be auto-passivated in both solutions and the passive current density increased about 2 order magnitude compared with cast alloy.In solution containing Cl~-,the passivity region of NC is 2 times than that of cast alloy.It indicated that the pitting resistance of NC was greatly improved.The semiconducting properties of the passive films formed on NC and cast alloy in both solutions were investigated by capacitance measurements.The results showed that Fe-20Cr cast alloy has poor resistance to pitting corrosion in chloride acidic solution due to its p-type semiconducting passive film.However,the passive film on Fe-20Cr NC was a n-type semiconductor which had a higher transpassivation potential and therefore higher resistance to pitting corrosion.The passive current density of NC was higher because of the higher donor/acceptor density in the passive film.The investigations showed that the type of passive films is responsible for the electrochemical behavior difference between NC and cast alloy.