Abstract:Arrays of well-aligned ZnO nanorods have been grown on Si substrates at 600 degrees C using a catalyst-free pulsed laser deposition (PLD) method, with and Without pre-deposition of a thin ZnO layer at a lower substrate temperature. Deposited products were analyzed and characterized by scanning and transmission electron microscopy (SEM and TEM), energy dispersive X-ray analysis, X-ray diffraction and photoluminescence (PL) measurements. EM revealed that rods grown directly on Si exhibit needle-like morphologies, with diameters, d, typically in the range 20-60 nm, lengths similar to 200-800 nm and, in most cases, capping particles of similar cross-section at their tips. HRTEM images show that these nanoparticles are ZnO also, suggesting that these derive from post-growth crystallisation of oxygen rich molten zinc droplets that cap the nanorods during growth. PLD of ZnO onto Si substrates that have been pre-coated with a thin ZnO film deposited at 300 degrees C yields denser, more uniform arrays of longer (similar to 1-1.2 mu m), thinner (d similar to 6-20 nm) nanorods, without any obvious capping particle. This suggests that a ZnO buffer layer can play a useful role in providing a high density of nucleation sites for subsequent growth of smaller diameter nanorods. The respective product arrays are most readily understood in terms of vapor-liquid-solid (V-L-S) and vapor-solid (V-S) growth models, respectively. Comparative studies of the room temperature PL from the respective samples reveal much higher UV emission intensity from nanorod arrays grown on the ZnO pre-coated Si substrates. (C) 2005 Elsevier Ltd. All rights reserved.

Growth of ZnO Hexagonal Nanoprisms

Zinc Oxide Nanostructures: Epitaxially Growing from Hexagonal Zinc Nanostructures

4 Nm ZnO Nanocrystals Fabrication Through Electron Beam Irradiation on the Surface of a ZnO Nanoneedle Formed by Thermal Annealing

Pinpoint Growth Mechanism of ZnO Nanoprisms

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

An “edge to Edge” Jigsaw-Puzzle Two-Dimensional Vapor-Phase Transport Growth of High-Quality Large-Area Wurtzite-Type ZnO (0001) Nanohexagons

Direct Observation of the Layer-by-Layer Growth of ZnO Nanopillar by In situ High Resolution Transmission Electron Microscopy

Growth Mechanisms for ZnO Nanorods Formed by Pulsed Laser Deposition

Nanocrystalline/nanoporous ZnO Spheres, Hexapods and Disks Transformed from Zinc Fluorohydroxide, Their Self-Assembly and Patterned Growth

Single-crystalline Zn2SnO4 Hexangular Microprisms: Fabrication, Characterization and Optical Properties

Controllable Growth of Laterally Aligned Zinc Oxide Nanorod Arrays on A Selected Surface of the Silicon Substrate by A Catalyst-Free Vapor Solid Process - A Technique for Growing Nanocircuits

Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation

Wet Chemical Approaches to Patterned Arrays of Well-Aligned ZnO Nanopillars Assisted by Monolayer Colloidal Crystals

Growth and Interconversion of ZnO Nanostructure Films on Different Substrates

Growth of aligned ZnO nanorod arrays by catalyst-free pulsed laser deposition methods

Lateral Growth and Optical Properties of ZnO Microcrystal on Sapphire Substrate

Large-scale hexagonal-patterned growth of aligned ZnO nanorods for nano-optoelectronics and nanosensor arrays

Studies on the Synthesis and Growth Mechanism of Single Crystal ZnO Nanowires

Aggregation-induced growth of hexagonal ZnO hierarchical mesocrystals with interior space: Nonaqueous synthesis, growth mechanism, and optical properties

Regrowth of template ZnO nanowires for the underlying catalyst-free growth mechanism

Continuous Growth Synthesis of Zinc Oxide Nanocrystals with Tunable Size and Doping