Abstract:Template process is of importance in the preparation of voided inorganic microspheres. In this paper, monodispersed polystyrene (PSt) template particles with diameter of 360 nm and surface carboxyl groups was first synthesized via batch soap-free emulsion copolymerization of styrene and methacrylic acid, and the core-shell PSt/SiO2 composite microspheres with variable shell thickness were prepared by surface modification-precursor method (PHC) and layer by layer method (LBL), respectively, and the voided SiO2 microspheres were finally obtained by calcining the PSt/SiO2 composite microspheres at 500°C for 4 h. The morphology of the microspheres was characterized on transmission electron microscopy (TEM) and scanning electron microscope (SEM). In the PHC method, when the PSt template particles were first modified with γ-aminopropyl triethoxysilane (KH-550) followed by reaction with tetraethoxysilane (TEOS) in the mixture medium of ethanol and water, the voided SiO2 microspheres with controllable uniformly compact shell thickness and smooth surface were received by calcining. However, the voided SiO2 microspheres resulted from LBL method were easy broken up because of their incompact shell structure, and their surface was much rough. In comparison, PHC method was much easier and more suitable than LBL method in the manufacture of voided SiO2 microspheres via template process.

Preparation of ordered macroporous CeO_2 balls by sol-gel templating method

Preparation of Ordered Macroporous Y_2O_3 Balls by Sol-Gel Templating Method

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Study on Preparation of Ordered Macroporous SiO_2 Balls

Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Controllable synthesis of spherical cerium oxide particles

Synthesis Of Ceo2 Spherical Fine Particles By Homogeneous Precipitation Method With Polyethylene Glycol

Study on preparation of ordered porous cordierite with colloidal crystals template

Shape-controlled synthesis of CeOHCO3 and CeO2 microstructures

Preparation of CeO2 Nanocrystals by Solvothermal Routes

Template Effects of the Ordered Film Formed from Monodispersed Polystyrene Latex

Fabrication of Ordered Porous Arrays Through in Situ Conversion Method Using Poly(Styrene-Co-Methacrylic Acid) Copolymer Colloidal Crystals

Study on porous TiO_2 thin film with colloidal crystals as template

The preparation of ceria colloids dispersed by polyvinyl alcohol

Preparation of cerium dioxide microspheres by internal gelation with cerium citrate as precursor

Synthesis and Characterization of Three-Dimensionally Ordered Macroporous Silica

Preparation of Ce-Mo complex oxide ultrafine particle catalyst by sol-gel method

Preparation with A Facile Template-Free Method of Uniform-Sized Mesoporous Microspheres of Rare Earth (la, Ce, Pr, Nd) Oxides

Fabrication of Binary Colloidal Crystals and Complex Ordered Mesoporous Silica Films Via Sol-Gel Technology

Influence of preparation method on the morphology of voided SiO2 microspheres prepared by template process

Highly Ordered Macroporous Au and Pd by Colloidal Crystal Templating