Abstract:In order to use lignosulfonates, a byproduct of Pulp and paper processes. as an effective water reducer, the physicochemical properties of calcium lignosulfonate (CL) with different molecular weights were investigated. It was found that the adsorptive capacity on the surface of cement particles, surface activity and foam production of CL increase with increasing its molecular weight however, the zeta potential and hence surface charge of the cement particles show highest values at the CL lower molecular weight fraction (5000-10.000). The physicochemical properties were related to some of the most important concrete performance properties. When the dosage of CL is less than 0.5 wt.% of the cement, the CL fraction with a molecular weight of 10,000-30,000 gives a maximum fluidity in the cement paste. The CL fraction of a high molecular weight has a stronger air-entraining effect, and hence decreases the compressive strength of concrete. Because there exist intrinsic limitations with CL as a water reducer (none of CL fractions can give good results on both fluidity and compressive strength), the original CL was further chemically modified into GCL1 by increasing its sulfonic groups, resulting in an average molecular weight around 10,000. This new compound gives to an increase in its charge density. and hence a higher zeta potential in its absolute value. Compared with CL, the surface tension of GCL1 solutions is lower, indicating possibly stronger wettina capability. GCL1 also has a larger adsorption capability on cement particles, and produces more hydrated ettringite needles in its microstructure. Furthermore. GCL1 shows comparable fluidity and compressive strength data to formaldehyde condensates (FDN), a gold standard of water reducer materials. This modified CL may be a potentially very useful water reducer. (c) 2005 Published by Elsevier B.V.

Study on Sulfonated Process of Pulp Black Liquor and the Application As Concrete Water Reducer

Study on Performance of Compound-modification Sulfonated Wheat Straw Lignin GSL As Water Reducer

Graft Sulfonation Process of Bamboo Pulp Black Liquor Used As Superplasticizer

Study on performance of activation sulfonation straw alkali lignin superplasticizer GSAL

Preparation of Lignosulfonate Water Reducer from Wheat Straw Alkali Lignin

Structural Characteristics of Sulfonated Wheat Straw Lignin from Alkali Pulping and Its Performances As Concrete Water-reducer

Investigation of Grafted Sulfonated Black Liquor As Wet‐ready Mortar Admixture

Effects of Water Reducer on the Properties of High-volume Fly Ash Cement Mortar

Ultrafiltration of Bamboo Pulp Black Liquor Modified by Graft Sulfonation and Water-Reducing Dispersion Performance of Fractions

Performance of Concrete Made with Superplasticizer from Modified Black Liquor and Polycarboxylate

Preparation of Lignin-Based Superplasticizer by Graft Sulfonation and Investigation of the Dispersive Performance and Mechanism in A Cementitious System

Effect of Modified Lignosulfonates Additive on Properties of Cement Mortar

Physicochemical Characterization of Calcium Lignosulfonate - A Potentially Useful Water Reducer

On Concrete Water Reducing Agent from Modified Lignosulfonate

Sodium Ligninsulfonate and Its Blendings with Polycarboxylic Superplasticizer

Effects of Different Kinds of Water-reducing Agents on Mechanical Performances of Mortar and Their Comprehensive Evaluation by Fuzzy Mathematics

Grafted-sulfonated Bamboo Pulping Liquor: Preparation and Property

Graft Sulfonation and Water Reducing-Performance Strengthening Effect of Acid Precipitation Lignin

Graft Copolymerization of Black Liquor and Sulfonated Acetone Formaldehyde and Research on Concrete Performance

Research on Compatibility of Graft-sulfonated Lignin As Superplasticizers

Study on Combination Use of Polycarboxylate Based Water Reducer and Lignosulphate Based Water Reducer