Abstract:Without use of any templates or shape-protectors, uniformly sized anatase TiO2 nanocrystallites with cuboidal morphology were synthesized by changing titanium hydroxide precipitates into their corresponding ethanol-gels (viz. by washing several times with anhydrous ethanol) followed by drying in supercritical ethanol (7.0MPa, 270°C) and calcination at high temperature (AS-preparation). Characterizations with X-ray diffraction (XRD), Raman spectroscopy and nitrogen adsorption suggest that the cuboidal anatase nanocrystallites are highly resistant to thermal sintering. The anatase structure of the cuboidal nanocrystallites was maintained even after calcinations up to temperatures as high as 800°C. Thermogravimetric (TG) measurements in flowing air show that the as-prepared cuboidal TiO2 nanocrystallites were contaminated with some carbonaceous residues, which can be completely removed by calcination at 500°C in air. Application of these cuboidal TiO2 nanocrystallites as photocatalytic materials was evaluated by photocatalytic degradation of methyl orange in water. With increasing the calcination temperature up to 800°C, the photocatalytic activities of anatase TiO2 cuboids increased gradually due to improved crystallization of the material. The sample calcined at 800°C afforded the highest photocatalytic activity, which is comparable to that of the commercial photocatalyst Degussa P-25. Due to the presence of carbonaceous residues after the supercritical drying in the preparation, the samples calcined at temperatures no higher than 400°C showed higher photocatalytic activities than the sample calcined at 500°C. However, further calcination of the sample at 1000°C led to drastic reduction in the photocatalytic activity due to the anatase-to-rutile phase transformation and sintering of the material.

Preparation and characterization of a titanium-substituted hydroxyapatite photocatalyst

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

Preparation of Nanocrystals Hydroxyapatite/tio2 Compound by Hydrothermal Treatment

Hydrothermal Synthesis and Photocatalytic Property of CaTiO_3 Assisted with Sodium Citrate

Ti-Modified Hydroxyapatites: Synthesis, Crystal Chemistry, and Photocatalytic Activity

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Hydrothermal synthesis of nano-sized titania and its photocatalytic activity

Influence of Hydrothermal Temperature on Structural and Photocatalytic Activity of Titanium Dioxide

Preparation And Photo-Catalytic Activity Of Tm Doped Tio2 Nanoparticles

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Low-Temperature Preparation And Characterization Of Nanosized Crystalline Anatase Titania With Titanium Tetrachloride And Acetic Anhydride As Materials

Effects of Hydrothermal Crystallization on the Morphologies and Photocatalytic Activity of TiO2 Nanotubes

Carbon-doped titania nanoplates with exposed {001} facets: facile synthesis, characterization and visible-light photocatalytic performance

Preparation of Titanium Dioxide Nanocrystallite with High Photocatalytic Activities

Hydrothermal synthesis and photocatalytic property of nanosized titania powders