Comparison of the effects of Mg and Zn on the interface mismatch and compression properties of 50 vol% TiB2/Al composites
Hong-Yu Yang,Zhong-Jie Cai,Qun Zhang,Yong Shao,Bai-Xin Dong,Qian-Qian Xuan,Feng Qiu
DOI: https://doi.org/10.1016/j.ceramint.2021.04.234
IF: 5.532
2021-08-01
Ceramics International
Abstract:<p>Low ductility limits the extensive application of high volume fraction (>30 vol%) ceramic particle-reinforced metal matrix composites, and the simultaneous improvement of strength and ductility is still a challenge owing to the smaller amount of matrix contained in such composites. In this paper, the effects of various contents of Mg or Zn (0, 6, 10 and 14 wt%) on the interface mismatch and compression properties of 50 vol% TiB<sub>2</sub>/Al composite fabricated in situ are comparatively studied. The results indicate that Mg has a better refinement effect than Zn on the TiB<sub>2</sub> ceramic particles. Mg can reduce the crystallographic mismatch degree of the Al/TiB<sub>2</sub> interface. 6 wt% Mg simultaneously increases the <em>σ</em><sub>0.2</sub>, <em>σ</em><sub>UCS</sub> and <em>ε</em><sub>f</sub> of the composite into 780 MPa, 1162 MPa and 10.68%, compared with the composite without the addition of Mg, increasing 8.5%, 2.8% and 30.6%, respectively. However, the addition of Zn leads to serious distortion of the Al lattice and deteriorates the interface matching degree of Al/TiB<sub>2</sub>, so the addition of Zn generally improves the <em>σ</em><sub>0.2</sub> and <em>σ</em><sub>UCS</sub> while sacrifices the plasticity simultaneously. Furthermore, the contributions of various strengthening mechanisms of the matrix in the high volume fraction TiB<sub>2</sub>/Al composites are analyzed through a comparative study.</p>
materials science, ceramics