Abstract:Superhydrophobic surfaces combining hierarchical micro/nanostructures were fabricated on zinc substrates by etching in hydrochloric acid solution, electrodeposition of ZnO coatings and subsequent thermal annealing. The optimal coatings were electrodeposited at -1.25 V for 900 s on the etched zinc substrates and then annealed at 200 degrees C for 60 min, which could achieve a maximum water contact angle of 170 +/- 2 degrees and an ultra-low sliding angle of approximately 0 degrees. By conducting SEM and water CA analysis, we found that the morphology and wettability of prepared samples were controllable by the fabrication process. Interestingly, even without any additional modification, the samples prepared under different electrodeposition conditions (including Zn(CH3COO)(2) concentration from 5 mM to 40 mM and deposition time from 300 s to 1500 s) exhibited superhydrophobic character. The influences of the Zn(CH3COO)(2) concentration, deposition time, annealing temperature and annealing time on the wetting behaviors were also discussed in detail. Such superhydrophobic surfaces possess long-term stability, and good corrosion resistance as well as self-cleaning ability. In addition, the anti-icing properties of the ZnO films were investigated. These surfaces could be rapidly and reversibly switched between superhydrophobicity and superhydrophilicity by alternating UV illumination and dark storage or thermal annealing. The intelligent switchable surfaces with controllable wettability and morphology offer possibilities for chemical, biological, electronic and microfluidic applications. (C) 2015 Elsevier B.V. All rights reserved.

Preparation of superhydrophobic coatings on zinc as effective corrosion barriers.

Preparation of superhydrophobic coatings on zinc, silicon, and steel by a solution-immersion technique.

Fabrication of superhydrophobic surfaces on zinc substrates and their application as effective corrosion barriers

Super-hydrophobic film prepared on zinc as corrosion barrier

Preparation of superhydrophobic films on titanium as effective corrosion barriers

Super-hydrophobic film prepared on zinc and its effect on corrosion in simulated marine atmosphere

Fabrication of Repairable Superhydrophobic Surface and Improved Anticorrosion Performance Based on Zinc-Rich Coating

Fabrication of stable homogeneous superhydrophobic HDPE/graphene oxide surfaces on zinc substrates

Superhydrophobic Anticorrosive Phosphonate–Siloxane Films Formed on Zinc with Different Surface Morphology

Controlled Fabrication of NiO/ZnO Superhydrophobic Surface on Zinc Substrate with Corrosion and Abrasion Resistance

Fabrication and Corrosion Resistance of Superhydrophobic Hydroxide Zinc Carbonate Film on Aluminum Substrates

Robust Superhydrophobic SiO2/polydimethylsiloxane Films Coated on Mild Steel for Corrosion Protection

Preparation of Superhydrophobic Zno Films on Zinc Substrate by Chemical Solution Method

Constructing a robust ZIF-7 based superhydrophobic coating with the excellent performance in self-cleaning, anti-icing, anti-biofouling and anti-corrosion

Fabrication of superhydrophobic surfaces on zinc substrates

Superhydrophobic and corrosion-resistant of 2-methylimidazolezincsalt-based coating enhanced with silane modification

Controllable Wettability and Morphology of Electrodeposited Surfaces on Zinc Substrates

Controllable fabrication of stable superhydrophobic surfaces on iron substrates

A Facile Approach to Fabricate Superhydrophobic Zn Surface and Its Effect on Corrosion Resistance

Facile construction of superhydrophobic polydopamine-based film and its impressive anti-corrosion performance on zinc surface

Synthesis and Corrosion Behavior of ZnO/SiO2 Nanorod-Sub Microtube Superhydrophobic Coating on Zinc Substrate