Abstract:Amorphous and nanocrystalline soft magnetic materials have attracted much attention in the area of sensor applications. In this work, the magnetoimpedance (MI) effect of patterned soft ferromagnetic meander-shaped sensor elements has been investigated. They were fabricated starting from the cobalt-based amorphous ribbon using the lithography technique and chemical etching. Three-turn (S1: spacing s = 50 μm, width w = 300 μm, length l = 5 mm; S2: spacing s = 50 μm, width w = 400 μm, length l = 5 mm) and six-turn (S3: s = 40 μm, w = 250 μm, length l = 5 mm; S4: s = 40 μm, w = 250 μm and l = 8 mm) meanders were designed. The 'n' shaped meander part was denominated as "one turn". The S4 meander possesses a maximum MI ratio calculated for the total impedance ΔZ/Z ≈ 250% with a sensitivity of about 36%/Oe (for the frequency of about 45 MHz), and an MI ratio calculated for the real part of the total impedance ΔR/R ≈ 250% with the sensitivity of about 32%/Oe (for the frequency of 50 MHz). Chemical etching and the length of the samples had a strong impact on the surface magnetic properties and the magnetoimpedance. A comparative analysis of the surface magnetic properties obtained by the magneto-optical Kerr technique and MI data shows that the designed ferromagnetic meander-shaped sensor elements can be recommended for high frequency sensor applications focused on the large drop analysis. Here we understand a single large drop as the water-based sample to analyze, placed onto the surface of the MI sensor element either by microsyringe (volue range 0.5-500 μL) or automatic dispenser (volume range 0.1-50 mL).

Giant magnetoimpedance effect and voltage response in meander shape Co-based ribbon

Valve Behavior Of Giant Magnetoimpedance In Field-Annealed Co70fe5si15nb2.2cu0.8b7 Amorphous Ribbon

Giant magnetoimpedance effects applications and materials science in patterned Co-based ribbons with a meander structure

Enhancement of magnetoimpedance effect in Co-based amorphous ribbon with a meander structure

Giant magnetoimpedance effects in patterned Co-based ribbons with a meander structure

Optimized Giant Magnetoimpedance Effect In Amorphous And Nanocrystalline Materials

Enhanced Gmi Effect in A Co70fe5si15b10 Ribbon Due to Cu and Nb Substitution for B

Effect of Meander Structure and Line Width on Gmi Effect in Micro-Patterned Co-Based Ribbon

Giant Magnetoimpedance Effect in a Co-Based Microwire for Quick-Response Magnetic Sensor Applications

Ultra-large Giant Magnetoimpedance Effect by a 2D Square Spiral Amorphous Microwire

Large Enhancement of Gmi Effect in Polymer Composites Containing Co-Based Ferromagnetic Microwires

Design and characteristic analysis of giant magnetoimpedance sensor in Fe-based nanocrystalline ribbons

Comparison of magnetoimpedance behaviors in meander CoFeNiSiB amorphous ribbon for deformation sensing applications

Optimization of temperature stability and sensitivity of the giant magnetoimpedance effect in meander shaped Co-based amorphous ribbon using DC-biased current for sensor application

Effect of annealing orientation on the giant magnetoimpedance in micro-patterned Co-based ribbon

Magnetoimpedance Effect in FINEMET/Ni80Fe20 Composite Ribbons

Sensitivity Enhancement of Longitudinally Driven Giant Magnetoimpedance Magnetic Sensor Using Magnetoelastic Resonance

Magnetoimpedance Effect in the Ribbon-Based Patterned Soft Ferromagnetic Meander-Shaped Elements for Sensor Application

Preparation of meander thin-film microsensor and investigation the influence of structural parameters on the giant magnetoimpedance effect

Transverse, Longitudinal and Perpendicular Giant Magnetoimpedance Effects in a Compact Multiturn Meander NiFe/Cu/NiFe Trilayer Film Sensor

Optimization of Magnetoimpedance Effect in Co-based Ribbon by Laser Patterning for Sensor Arrays Application