Manipulation of microstructure evolution and deformation behavior in Ni–Mn–Ga shape memory alloys with varied Ni/Ga under uniaxial cyclic compression
Xin-Xiu Wang,Xin Ding,Rui-Run Chen,Jie-Fei Ding,Hong-Xian Shen,Ming-Fang Qian,Yong Zhang,Shi-Ping Wu
DOI: https://doi.org/10.1007/s12598-024-02982-5
IF: 6.318
2024-10-06
Rare Metals
Abstract:The regulation of martensitic transformation and intrinsic brittleness are critical issues for the application of Ni–Mn–Ga shape memory alloys, and they are closely related to the alloy composition and γ phase. In this study, single and dual-phase Ni 55+ x Mn 25 Ga 20− x ( x = 0, 2, 4 and 6) alloys were fabricated. The proportion of the γ phase was elevated gradually, and the peak martensitic transformation temperature was enhanced from 350 to 460 °C with an increasing Ni/Ga ratio. The microstructures of the γ phase were further regulated from continuous block to dispersed granular after annealing. The annealed dual-phase alloy with x = 2 exhibited greater yield stress, compressive strength and toughness than the annealed single-phase alloy. It maintained plastic deformation without fracture, even at a strain of 30%. High strain energy and dislocation density were observed in the martensite of the dual-phase alloy, which can be attributed to γ phases and the interface between martensite and γ phases. Furthermore, [001]-oriented martensite variants were obtained during deformation in the dual-phase alloy. They were parallel to the loading direction and conducive to improving the compressive strength. This protocol provides in-depth insight into the influence of the γ phase on the texture evolution and mechanical behavior of martensite during deformation.
materials science, multidisciplinary,metallurgy & metallurgical engineering