Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction
Nan Cui,Hangle Guo,Jian Zhou,Linghao Li,Limin Guo,Zile Hua
DOI: https://doi.org/10.1016/j.micromeso.2020.110411
IF: 5.876
2020-10-01
Microporous and Mesoporous Materials
Abstract:<p>In methanol-to-propylene reaction, the catalytic performance of ZSM-5 zeolite is strongly related to the material textural properties and surface acidity. In this work, the regulation of framework Al distribution (origin of the active Brønsted acid sites) in high-silica hierarchically structured ZSM-5 zeolite has been realized by a boron-modification procedure. When the B/Al ratio of the gel compositions (Si/Al = 200) reaches 7 or 9, the resultant B<sub>7</sub>- and B<sub>9</sub>-HSZ materials possess the expected hierarchically micro/mesoporous structures and increased framework Al distribution in the narrow straight/sinusoidal channels of MFI-type zeolite, which have been confirmed by the complementary characterizations, i.e. XRD, N<sub>2</sub> sorption isotherms, ICP-OES, SEM, TEM, <sup>27</sup>Al MAS NMR and the probe reaction of 1-hexene cracking. As a result, compared to the unmodified sample B<sub>0</sub>-HSZ and sample B<sub>3</sub>-HSZ with lower B-doping amount in the gels, they demonstrate the improved target propylene selectivity (49.3% and 48.9%) and elongated catalyst lifetime (88 h and 91 h) in MTP reaction under the WHSV of 2.8 h<sup>−1</sup>.</p>
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied