Homogeneously Co/Ce Co-Doped Amorphous MnOx Microspheres with Abundant Oxygen Vacancy for Catalytic Combustion of Propane
Jinyan Xiao,Chi Zhang,Yulong Wang,Pengfei Tu,Lei Yang,Shengwei Tang,Wenxiang Tang
DOI: https://doi.org/10.1016/j.fuel.2024.133631
IF: 7.4
2025-01-01
Fuel
Abstract:Developing simple and effective strategies to construct rich oxygen vacancies is of great importance for enhancing the catalytic efficiency of heterogeneous catalysts. This study prepared Ce and Co-doped manganese oxide catalysts with microsphere morphology by a simple and facile solvent-thermal reaction strategy, which were further applied for the catalytic combustion of chemically stable light alkane such as propane. The results of systematic characterizations verified that the incorporation of Ce and Co into MnOx generates more structural defects with abundant oxygen vacancies. The Mn3(Co2Ce1)1 catalyst, which was obtained by Co, Ce co-doping, possessed the highest content of oxygen vacancies as well as strengthened physic-chemical features such as larger specific surface, more surface-active species, better redox capacity, enhanced oxygen mobility and acidity. As a result, this sample displayed superior low-temperature catalytic activity, achieving 90 % conversion of propane at 263 °C under high space velocity (120,000 mL·gcat-1·h−1), which was 87 °C lower than that of pure manganese oxide. Moreover, in-situ DRIFTS was also employed to reveal the possible pathways of propane degradation over the Mn3(Co2Ce1)1 catalyst. Meanwhile, clear improvements reflected in thermal stability and resistance to water were also realized by modifying Co and Ce, showing great potential for practical industrial applications.