Formation mechanism of recrystallisation internal friction peak and its application to determine the recrystallisation temperature of deformed pure Cu
Tianlu Chen,Meng Sun,Run Yang,Rui Liu,Weibin Jiang,Tao Zhang,Xuebang Wu,Xianping Wang,Changsong Liu,Qianfeng Fang,Tianlu ChenMeng SunRun YangRui LiuWeibin JiangTao ZhangXuebang WuXianping WangChangsong LiuQianfeng Fanga Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,Hefei,People's Republic of Chinab University of Science and Technology of China,Hefei,People's Republic of Chinac School of Physics and Materials Science,Guangzhou University,Guangzhou,People's Republic of ChinaTianlu Chen is a Graduate student in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Meng Sun is an Associate Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Run Yang is a Graduate student in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Rui Liu is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Weibin Jiang is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Tao Zhang is a Professor in the School of Physics and Materials Science,Guangzhou University,China.Xuebang Wu is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Xianping Wang is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Changsong Liu is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.Qianfeng Fang is a Professor in the Key Laboratory of Materials Physics,Institute of Solid State Physics,HFIPS,Chinese Academy of Sciences,China.
DOI: https://doi.org/10.1080/09500839.2024.2302628
IF: 1.195
2024-02-01
Philosophical Magazine Letters
Abstract:The formation mechanism of a recrystallisation internal friction (IF) peak superimposed on a grain boundary (GB) IF peak for deformed copper was studied. The P 1 peak, associated with the recrystallisation process, was observed at ∼ 599 K (2 K/min) during the first heating process. Subsequently, the P 2 peak, located at ∼ 510 K (0.2 Hz), corresponded to GB relaxation during the cooling process. The P 1 peak showed minor relaxation at higher frequencies owing to the influence of GB relaxation. To accurately determine the temperature of the P 1 peak in this scenario, two methods were used: fitting the measured IF spectra and performing IF measurements at lower frequencies and/or with faster heating rates to minimise the impact of GB relaxation. This work investigated the formation mechanism of the recrystallisation peak and supplemented the method for determining the recrystallisation temperature through IF measurements when the GB peak occurs at a nearby temperature.
materials science, multidisciplinary,physics, applied, condensed matter,metallurgy & metallurgical engineering