Abstract:A composite titania thin film consisted of quasi-aligned single-crystalline rutile nanorods embedded in sol-gel-derived anatase aggregates was fabricated and its photoelectrochemical behavior was studied in detail. A monolayer of nearly sing I e-crystal line rutile nanorods was first deposited on metallic Ti substrates through a controlled reaction between Ti and hydrogen peroxide. The gaps among the rutile nanorods were then filled with titania nanoparticles through a sol-gel dip-coating approach, which achieved a composite thin film of single-crystalline rutile nanorods embedded in anatase aggregates, after a subsequent thermal treatment at 723 K. The X-ray diffraction measurement revealed that the composite film with thickness of 180 nm contained anatase and rutile in a nearly 50:50 ratio. The UV-visible diffusive reflectance spectra estimated a band gap of 2.99 eV for the rutile monolayer and a slightly increased value of 3.03 eV for the composite film due to the embedding of the anatase nanoparticles. Photocurrent versus potential diagrams, photocurrent transient curves, and open-circuit potential measurement supported the fact that the anatase nanoparticles possessed better inherent photoelectrochemical properties than rutile. However, electrochemical impedance spectra characterization, together with photocurrent transient curves and open-circuit potential measurement, suggests that the single-crystalline rutile nanorods exhibited a higher electron-transfer rate. The combination of the two components in such an appropriate way enhanced significantly the charge separation effect arising from the anatase/rutile couple, which hence combined efficiently the "mixed crystal effect" and the "mixed morphological effect". A steady-state photocurrent more than double the simple sum of those generated by the two components alone was detected for the current composite film, which can be attributed to the single-crystalline rutile nanorods that provide channels for rapid electron transfer to the conductive Ti substrates under an applied bias potential. As a result, this study concludes that the present nanostructure magnified significantly the well-established mixed crystal effect, that is, an enhanced charge separation arising from a mixture of anatase and rutile.

Photoelectric Behavior of Nanocrystalline TiO2 Electrode with a Novel Terpyridyl Ruthenium Complex

Novel Cyanine Dyes with Different Methine Chains As Sensitizers for Nanocrystalline Solar Cell

Synthesis of Rhenium(I) Bipyridyl and Ruthenium(Ii) Tris-Bipyridyl Photosensitive Dyes Used for Solar Cells

Photocurrent Enhancement by Employing 2,6-Bis[1-(2,4,6-trimethyl-phenylimino)ethyl]Pyridine as a Co-Sensitizer with Ruthenium in Dye Sensitized Solar Cell

Effects of rubrene co-sensitized TiO 2 photoanode on the performance of ruthenium dye N719 sensitized solar cells

Enhance the performance of dye-sensitized solar cells by co-sensitization of 2,6-bis(iminoalkyl)pyridine and N719

Enhanced photovoltaic performance of dye-sensitized solar cells using a new photoelectrode material: upconversion YbF3-Ho/TiO2 nanoheterostructures

Photoelectric Conversion Properties of Nanocrystalline Tio2 Electrodes Sensitized with Hemicyanine Derivatives

Highly Efficient Charge Transfer From A Trans-Ruthenium Bipyridine Complex To Nanocrystalline Tio2 Particles

The Sensitization of Nanoporous TiO2 Electrodes by Porphyrin Derivatives with Different Substituents

Significant Influence of TiO2 Photoelectrode Morphology on the Energy Conversion Efficiency of N719 Dye-Sensitized Solar Cell

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

Photosensitization of ITO and nanocrystalline TiO2 electrode with a hemicyanine derivative

Terpyridyl Ruthenium Complexes Functionalized with Conjugated Heterocycles for Panchromatic Dye-Sensitized Solar Cells

Ruthenium(II) complex based on 4,4′-di(p-methylphenyl)-2,2′-bipyridine: Synthesis and photoelectrochemical properties

Enhanced Photoelectrochemical Response of a Composite Titania Thin Film with Single-Crystalline Rutile Nanorods Embedded in Anatase Aggregates

Enhanced Energy Conversion Efficiency of the Sr2+-Modified Nanoporous Tio2 Electrode Sensitized with A Ruthenium Complex

A Highly Efficient Solar Cell Made from A Dye-Modified Zno-Covered Tio2 Nanoporous Electrode

Enhance the Optical Absorptivity of Nanocrystalline TiO2 Film with High Molar Extinction Coefficient Ruthenium Sensitizers for High Performance Dye-Sensitized Solar Cells.

The photoelectrochemical properties of dye-sensitized solar cells made with TiO2 nanoribbons and nanorods

Bifunctional Single-Crystalline Rutile Nanorod Decorated Heterostructural Photoanodes For Efficient Dye-Sensitized Solar Cells