Abstract:The poor wear and corrosion resistance of Mg alloys are hampering wider application. Micro-arc oxidation can improve the wear and corrosion resistance, but the resulting coatings have relatively low hardness, high friction coefficient, and surface porosity, rendering them susceptible to failure in the field. Herein, ZrO(2 )nanocrystalline and extrinsic graphite-doped MAO coatings are prepared on the ZK61 Mg alloy using a control electrolyte containing potassium fluorozirconate and nano-graphite. The ZrO2 nanocrystals formed in situ are uniformly distributed in the amorphous coating, while the extrinsic graphite is mainly located in the amorphous structure. The size and number of pores decrease after introducing ZrO2 and graphite into the MAO coating. Compared with doping with a single element, co-doping increases the content of ZrO2 and graphite in the MAO coating. Furthermore, ZrO2 2 densifies the porous Mg(OH)2 2 corrosion product and blocks the penetration of the corrosive medium to improve the corrosion resistance. The optimized sample shows corrosion potential and corrosion current density of-1.012 V and 1.425 x 10-7A center dot cm-(- 7) A center dot cm(- 2) , which are significantly better than the singly doped MAO coating. Graphite doping decreases the friction coefficient, while ZrO2 2 doping decreases the wear rate. The ZrO2 and graphite co-doped C10Zr10 coating demonstrates self-lubricating properties, resulting in a significantly reduced wear rate from 2.832 x 10(-4) mm(3)center dot N-1 center dot m(- 1) to 1.04 x 10(-5)mm(3)center dot N-1 center dot m(- 3 )center dot N- 1 center dot m(- 1) . The results reveal that co- doping improves the properties of MAO coatings on Mg alloys.

Tribological Properties of MAO Coating with Nano-graphite on ZM5 Magnesium Alloy

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Improved Lubricating and Corrosion Resistance of MAO Coatings on ZK61 Mg Alloy by Co-Doping with Graphite and Nano-Zirconia

Study on Structure and Properties of Microarc Oxidation Coating Formed on AM60B Magnesium Alloy

Preparation and properties of nano ZrO2 coating on magnesium alloy

Effect of Several Inorganic Additives on Microstructure and Properties of Microarc Oxidation Coating on Aluminium Alloy

Effect of micro-groove on microstructure and performance of MAO ceramic coating fabricated on the surface of aluminum alloy

Friction and Wear Behavior of Graphene-Modified Titanium Alloy Micro-arc Oxidation Coatings

Study on the Optimization of the Preparation Process of ZM5 Magnesium Alloy Micro-Arc Oxidation Hard Ceramic Coatings and Coatings Properties

Effect of Graphite Content on the Conductivity, Wear Behavior, and Corrosion Resistance of the Organic Layer on Magnesium Alloy MAO Coatings

Corrosion and tribocorrosion resistance of MAO-based composite coating on AZ31 magnesium alloy

Preparation, interface properties and corrosion behavior of nano-modified MAO ceramic film on 5B70 Al alloy

Oxide ceramic coatings with amorphous/nano-crystalline dual-structures prepared by micro-arc oxidation on Ti–Nb–Zr medium entropy alloy surfaces for biomedical applications

Influence of nanoparticle additions on structure and fretting corrosion behavior of micro-arc oxidation coatings on zirconium alloy

Study on the wear resistance and corrosion behaviour of self-sealed MAO/ZrO 2 coatings prepared on 7075 aluminium alloy

Friction Reduction of Aluminum Alloy Micro-arc Oxidation Coating by Filling Graphene Oxide

Tribological and corrosion resistance properties of graphite composite coating on AZ31 Mg alloy surface produced by plasma electrolytic oxidation

The influence of rolling on the corrosion and wear resistance of the MAO coating on ZM5 alloy

Ceramic coatings by microarc oxidation of Ti and Al alloys

Effect of Na2 WO4 on properties of micro-arc oxidation ceramic coatings on aluminum alloy

Effect of Nano-ZrO2 on the Microstructure and High Temperature Tribological Properties of MoSi2 Coating