Alrik Durand,Yoann Baron,Péter Udvarhelyi,Félix Cache,Krithika V.R.,Tobias Herzig,Mario Khoury,Sébastien Pezzagna,Jan Meijer,Jean-Michel Hartmann,Shay Reboh,Marco Abbarchi,Isabelle Robert-Philip,Adam Gali,Jean-Michel Gérard,Vincent Jacques,Guillaume Cassabois,Anaïs Dréau
2024-04-23
Abstract:Among the wealth of single fluorescent defects recently detected in silicon, the G center catches interest for its telecom single-photon emission that could be coupled to a metastable electron spin triplet. The G center is a unique defect where the standard Born-Oppenheimer approximation breaks down as one of its atoms can move between 6 lattice sites under optical excitation. The impact of this atomic reconfiguration on the photoluminescence properties of G centers is still largely unknown, especially in silicon-on-insulator (SOI) samples. Here, we investigate the displacement of the center-of-mass of the G center in silicon. We show that single G defects in SOI exhibit a multipolar emission and zero-phonon line fine structures with splittings up to $\sim1$ meV, both indicating a motion of the defect central atom over time. Combining polarization and spectral analysis at the single-photon level, we evidence that the reconfiguration dynamics are drastically different from the one of the unperturbed G center in bulk silicon. The SOI structure freezes the delocalization of the G defect center-of-mass and as a result, enables to isolate linearly polarized optical lines. Under above-bandgap optical excitation, the central atom of G centers in SOI behaves as if it were in a 6-slot roulette wheel, randomly alternating between localized crystal sites at each optical cycle. Comparative measurements in a bulk silicon sample and ab initio calculations highlight that strain is likely the dominant perturbation impacting the G center geometry. These results shed light on the importance of the atomic reconfiguration dynamics to understand and control the photoluminescence properties of the G center in silicon. More generally, these findings emphasize the impact of strain fluctuations inherent to SOI wafers for future quantum integrated photonics applications based on color centers in silicon.
Quantum Physics