Radioluminescence of Ce3+-doped B2O3–SiO2–Gd2O3–BaO glass

Chun Jiang,Peizhen Deng,Junzhou Zhang,Fuxi Gan

DOI: https://doi.org/10.1016/j.physleta.2004.01.038

IF: 2.707

2004-01-01

Physics Letters A

Abstract:The object of this work is to explore the possibility of cerium-doped dense oxide glasses as dense scintillator for medical imaging application. Large block Ce3+-doped 30SiO2–25B2O3–30Gd2O3–15BaO glass was prepared and the radioluminescence, photoluminescence and decay time were measured, and its scintillation properties such as scintillation light output, attenuation length, decay time and radiation hardness were analyzed. It was observed that peak scintillation light intensity of present glass doped with 5.0 wt.% Ce2O3 is 13% of that of BGO, and its decay time was in range of 60–80 ns, glass density was near 5.40 g/cm3. It is concluded that the trivalent cerium-doped oxide glass scintillator with low cost and availability in large scale and good chemical durability might become one of promising candidates of cerium-doped dense scintillator for medical imaging application.