Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

A Novel Approach for Preparation of Y2O3:Eu3+ Nanoparticles by Microemulsion–microwave Heating

Hydrothermal Synthesis and Upconversion Luminescence of Yb3+/Er3+ Co-doped BaY2F8 Nanoparticles

Efficient route for preparation of Nd3+ doped Y2O3 nanoparticles at intermediate temperature

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Low temperature chemical reaction synthesis of single-crystalline Eu(OH)<sub>3</sub> nanorods and their thermal conversion to Eu<sub>2</sub>O<sub>3</sub> nanorods

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Characterization of europium doped yttrium nano-oxide prepared by plasma electrolysis in nitrate solution under air atmosphere at room temperature

General and Facile Method To Prepare Uniform Y<sub>2</sub>O<sub>3</sub>:Eu Hollow Microspheres

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Using different ratios of glycine to citric acid as fuel mixture in microwave-assisted combustion synthesis of Eu-doped Y2O3–Gd2O3 nanophosphors

Preparation of Yvo4:Re (re=yb3+/er3+, Yb3+/Tm3+) Nanoparticles Via Microemulsion-Mediated Hydrothermal Method

Citrate-mediated hydrothermal route to synthesis a large-scale Y2O3 : Eu3+ hexangular prism

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Preparation and Optical Properties of YH2:Er2+ and Y2O3:Er3+ Nanoparticles.

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Optimization of photoluminescence of Eu3+ doped YVO4 nanoparticles by green microwave synthesis

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Synthesis and photoluminescence of Eu3+-doped Y2Sn2O7 nanocrystals

Preparation Of Europium (Iii) Doped Nanocrystalline Zinc Oxide In Ionic Liquid Via An Ultrasonic Irradiation

Preparation of Eu3+-doped rutile TiO2 nanocrystals at room temperature by a sonochemical method