Abstract:Enhancing the thermal shock resistance of Y2O3 ceramic crucibles, coupled with advancements in melting and casting technologies to reduce the adverse influence of interfacial reactions, is essential for producing low-energy consumption, high-quality titanium-aluminum (TiAl) alloys. In this study, the Y2O3 ceramic crucible with good thermal shock resistance was developed through the optimization of particle size distribution and sintering holding time. The interaction mechanisms between Y2O3 ceramics and TiAl alloys under extreme conditions were investigated, and strategies for enhancing the mechanical properties of TiAl alloys through the integration of Y2O3 crucibles with centrifugal casting were discussed. The results indicated that introducing large particles of 1-3 mm under sintering conditions of 2023 K and 6 h effectively enhances the thermal shock resistance of Y2O3 crucible. The interaction between Y2O3 and TiAl alloys primarily involved physical erosion (spalling/dispersion), dissolution of separated particles, and surface modification of interface layer particles (reaction). Physical erosion played an important role in this dynamic interaction, with the extent of erosion intensifying through continuous use of the crucible, while electromagnetic forces ensured the uniform distribution of inclusions within the TiAl alloy matrix. Moreover, the application of centrifugal casting technology substantially refines the grain size and reduces the inclusion count, thereby significantly enhancing the mechanical properties of TiAl alloy.

Interfacial Reaction between Ti-47Al-2Cr-2Nb Alloy Melt and Y2O3 Shell Mold

Interface interaction during the preparation of TiAl-(Nb, V) quaternary intermetallic single crystals by directional solidification based on Y2O3 doped BaZrO3/Al2O3 composite ceramic mold

Microstructure formation and interface characteristics of directionally solidified TiAl-Si alloys in alumina crucibles with a new Y 2 O 3 skull-aided technology

Effect of Aluminum Content on Interfacial Reaction of Directionally Solidified TiAl Alloys

Lnterfacial reaction between TiAl base alloy melt and oxide mould

Comparison of a Directionally Solidified TiAl Alloy by Φ15 Mm Cylindrical and 29 × 6 Mm Plate Y 2 O 3 Molds

Interface Reaction Between Ceramic Moulds and Ti46al1b As-Cast Valves

Understanding the Metal-Mold interfacial reactions during directional solidification of superalloys using Al 2 O 3 -rich ceramic mold

The Study on Interaction Mechanisms Between Ti48al2cr2nb Alloy and Y2o3 Ceramic Crucibles with Good Thermal Shock Resistance: Assessing a Novel, Cost-Effective Approach to the Preparation of High-Performance Tial Alloys

A Novel Directional Solidification Of Tial-Based Alloys By Electromagnetic Cold Crucible Zone Melting Technology With Y2o3 Moulds

Interface Reaction During Titanium Alloys Investment Casting by Residue Gas in Ceramic Mold

Reaction between Ti–6Al–4V and Y 2 O 3 –SiO 2 based face shell for investment casting

Study of Interfacial Reaction Between TiAl Alloys and Four Ceramic Molds

Interfacial reactions between Ti-1100 alloy and ceramic mould during investment casting

Microstructure and interface reaction of titanium alloys casting into different mould shells

Effects of pouring temperature on interfacial reaction between Ti-47.5Al-2.5V-1Cr alloy and mold during centrifugal casting

Microstructural Control and Mechanical Properties of Ti–47Al–2Cr–2Nb Alloy by Directional Solidification Electromagnetic Cold Crucible Technique

Microstructure and Interface Reaction of Investment Casting Tial Alloys

High-temperature wetting behavior of molten Ni-based superalloy on Y2O3 ceramics with different surface microstructures

The Directional Solidification, Microstructural Characterization and Deformation Behavior of Β-Solidifying TiAl Alloy

Interface reaction between TiNi alloy and BN based shell mold for investment casting Ti alloy