Synthesis and Characterization of Biodegradable Poly(Lactic Acid-Co-Glycine) Via Direct Melt Copolymerization
Zhaoyang Wang,Xiaona Hou,Zhengzhou Mao,Ruirong Ye,Yangqing Mo,David E. Finlow
IF: 2.485
2008-01-01
Iranian Polymer Journal
Abstract:Instead of the traditional two-step method with cyclic intermediates, a direct reaction of D,L-lactic acid (D,L-LA) and glycine (Gly) as monomers (molar feed ratio LA/Gly: 90/10) and SnO (0.7 wt%) as catalyst is carried out to synthesize a biodegradable poly(lactic acid-co-glycine) [P(LA-co-Gly)] via melt copolycondensation at 170 degrees C, absolute pressure of 70 Pa, for 8 h, following a prepolymerization step. The structure of the copolymer was characterized by FTIR and H-1 NMR techniques. The GPC results show that the weight average molecular weight ((M) over bar (w)) of the copolymer P(LA-co-Gly) is 3600 g/mol. Under the condition of different molar feed ratios the highest (M) over bar (w) was found to be 5200 with molar feed ratio LA/Gly:98/2. Other characterizations, e.g., intrinsic viscosity, solubility, DSC, and XRD indicated that the copolymer solubility in chloroform and tetrahydrofuran (THF) decreased with the increasing feed charge of Gly and the lowest solubility was found when the molar feed ratio was below LA/Gly:70/30. However, the modified polylactic acid is readily soluble in DMSO. The crystallinity of copolymer gradually disappears as the molar feed ratio of D,L-LA decreases. For LA/Gly >= 90/10, the XRD pattern has two diffraction peaks, close to 16.8 degrees and 19.1 degrees, the same position as poly(D,L-lactic acid) (PDLLA). For the soluble P(LA-co-Gly) the intrinsic viscosity, (M) over bar (w) and its dispersity ((M) over bar (w)/(M) over bar (n)) decrease gradually with the increase of feed charge of Gly. These results, especially the molecular weight of the copolymer appear to meet the requirements necessary for a drug delivery applications.