Abstract:NaA zeolite membranes were successfully synthesized on a porous α-Al2O3 support from clear solution. The synthesis parameters, such as surface seeding, synthesis time, synthesis stages, etc. were investigated. Surface seeding can not only accelerate the formation of NaA zeolite on the support surface, but can also inhibit the transformation of NaA zeolite into other types of zeolites. A continuous NaA zeolite membrane formed on the seeded support after 2 h of synthesis. Gas permeation results showed that a synthesis time of 3 h produced the best NaA zeolite membrane. When the synthesis time was longer than 4 h, the NaA zeolite on the support surface began to transform into other types of zeolites, and the quality of the NaA zeolite membrane decreased. The quality of the NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance. The permeances of H2, O2, N2, and n-C4H10 decreased as the molecular kinetic diameter of the gases increased, which showed the molecular sieving effect of the NaA zeolite membrane. The permselectivities of H2/n-C4H10 and O2/N2 were 19.1 and 1.8, respectively. These values are higher than the Knudsen diffusion ratios of 5.39 and 0.94. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects with diameters larger than the pore size of NaA zeolite. A synthesis model was proposed to clarify the effect of surface seeding.

Microwave Synthesis of Polyetherimide-NaA/α-Al_2O_3 Supported Zeolite Membrane

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Preparation of zeolite A membranes by microwave heating

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Ultrasonic Treatment of Polyacrylic Acid Sodium/Naa Zeolite Hybrid Membranes for the Pervaporation Dehydration of Ethanol

Preparation of Asymmetric Zeolite NaA Membrane Layers by Vapor Phase Transfer and Seeded Growth Method

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

High-Performance Zeolite Naa Membranes on Polymer-Zeolite Composite Hollow Fiber Supports

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Microwave-Assisted Synthesis of Naa Zeolite Membrane with High Separating Performance by Seeding Using Vpt Method

Influences of adding organic intermediate layer on membrane formation and properties

Manipulation of the Surface Microstructure and Its Effects on the Flux of NaA Zeolite Membranes in Pervaporation

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Synthesis of NaA zeolite membranes from clear solution

Zeolite NaA membranes supported on alumina hollow fibers: Effect of support resistances on pervaporation performance

Influences of the Zeolite Loading and Particle Size in Composite Hollow Fiber Supports on Properties of Zeolite Naa Membranes

A Novel Seeding Method of Interfacial Polymerization-Assisted Dip Coating for the Preparation of Zeolite NaA Membranes on Ceramic Hollow Fiber Supports.

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer