Abstract:Phosphoric acid (PA)-doped ion exchange membranes have been recognized as a classical high-temperature proton exchange membrane (HT-PEM) material. Nonetheless, the leaching of PA from membranes occurs progressively during operation, inevitably diminishing overall performance. In this study, we present a novel approach for crafting two-dimensional porous organic polymer nanosheets (NS-POPs) synthesized through nanointerfacial azo-coupling polymerization. The prepared NS-POPs possessed different pore structures with main pore sizes of 0.55 nm and 1.19 nm, which were derived from the discrepancy of monomer structure. Subsequently, the NS-POPs were successfully incorporated into polybenzimidazole to create mixed-matrix membranes due to the good interface compatibility, characterized by homogeneity and stability facilitated by the 2D nature of NS-POPs. As a comparison, POPs with non-2D properties prepared by the solution method cannot be successfully obtained in good MMMs due to poor dispersibility and interface compatibility. Furthermore, the profusion of pore structures and the presence of N/O-rich functional groups in NS-POPs significantly enhance their PA uptake capacity with up to 289 %, consequently boosting proton conductivity. As a result, the composite membrane doped with NS-POPs demonstrated a maximum conductivity of up to 143 mS cm-1 at 180 degrees C, which is approximately 2.97 times that of pure membrane. And the peak power density of H2/O2 fuel cell based on the composite membrane was 378 mW cm-2, which was higher than PBI. Most significantly, the confinement effect exerted by the small pores in NS-POPs enables composite membranes to maintain a higher PA retention of up to 74 % even after a 48 h of high-temperature and high-humidity treatment. Our study introduces an innovative and straightforward approach to synthesizing porous organic polymer nanosheets. This work not only advances the understanding of the impact of interface compatibility on composite membrane fabrication, but also establishes a versatile technology for modulating pore size and managing PA leaching in HT-PEMs.

Thermally Stable Sulfonated Nanoporous Aryl Epoxy Resin As Proton Exchange Membranes at Elevated Temperatures.

Proton Exchange Membranes Based on Aryl Epoxy Resin for Fuel Cells Operated at Elevated Temperatures

Sulfonated Polyaryletherketone with Pendant Benzimidazole Groups for Proton Exchange Membranes

Polybenzimidazole/ionic-liquid-functional Silica Composite Membranes with Improved Proton Conductivity for High Temperature Proton Exchange Membrane Fuel Cells

Gel-state Polybenzimidazole Proton Exchange Membranes with Flexible Alkyl Sulfonic Acid Side Chains for a Wider Operating Temperature Range (25–240 °C)

High ion exchange capacity perfluorosulfonic acid resine proton exchange membrane for high temperature applications in polymer electrolyte fuel cells

Composite proton exchange membrane featuring a three-layer structure: Enhanced thermal stability, proton conductivity, and fuel cell performance

Enhancing the Chemical Stability of Poly(isatin terphenyl)-Based Anion Exchange Membranes by Cross-Linking with Quaternary Ammonium-Functionalized Noria

Ionically Crosslinked Composite Membranes from Polybenzimidazole and Sulfonated Poly (fluorenyl ether ketone) for High-Temperature PEM Fuel Cells

High conductive and dimensional stability proton exchange membranes with an all-carbon main chain and densely sulfonated structure

Anion Exchange Membranes Based on Sulfonated Poly(ether ether ketone) Crosslinked Methylpyrrolidinium Functionalized Poly (vinyl benzyl chloride) with High Chemical Stability

Polyethyleneimine-Filled Sepiolite Nanorods Embedded Poly(2, 5-Benzimidazole) Composite Membranes for Wide Temperature PEMFCs

Tuned polymer electrolyte membranes based on aromatic polyethers for fuel cell applications

Multi-Block Copolymer Membranes Consisting of Sulfonated Poly(p-Phenylene) and Naphthalene Containing Poly(Arylene Ether Ketone) for Proton Exchange Membrane Water Electrolysis

Preparation of Graft Poly(Arylene Ether Sulfone)s-Based Copolymer with Enhanced Phase-Separated Morphology As Proton Exchange Membranes Via Atom Transfer Radical Polymerization

Incorporating 2D Porous Organic Polymer Nanosheets into High-Temperature Proton-Exchange Membranes for Low H3PO4 Loss

High Temperature PEM Fuel Cells Based on Nafion®/SiO2 Composite Membrane

Construction of Stable Wide‐Temperature‐Range Proton Exchange Membranes by Incorporating a Carbonized Metal–Organic Frame into Polybenzimidazoles and Polyacrylamide Hydrogels

Sulfonating and Polyhedral Oligomeric Silsesquioxane Crosslinking in One Step to Build Multiple Proton Pathways for Proton Exchange Membrane Fuel Cells over a Wide Temperature Range

Poly(2,5-benzimidazole)/sulfonated Sepiolite Composite Membranes with Low Phosphoric Acid Doping Levels for PEMFC Applications in a Wide Temperature Range

Advancements in proton exchange membranes for high-performance high-temperature proton exchange membrane fuel cells (HT-PEMFC)