Effects Of Melt Structure On Crystallization Behavior Of Isotactic Polypropylene Nucleated With Alpha/Beta Compounded Nucleating Agents
qiyan zhang,zhengfang chen,bing wang,jinyao chen,feng yang,jian kang,ya cao,ming xiang,huilin li
DOI: https://doi.org/10.1002/app.41355
IF: 3
2015-01-01
Journal of Applied Polymer Science
Abstract:In this study, the melt structure of isotactic polypropylene (iPP) nucleated with / compounded nucleating agents (/-CNA, composed of the -NA of 0.15 wt % Millad 3988 and the -NA of 0.05 wt % WBG-II) was tuned by changing the fusion temperature T-f. In this way, the role of melt structure on the crystallization behavior and polymorphic composition of iPP were investigated by differential scanning calorimetry (DSC), wide-angle X-ray scattering (WAXD) and scanning electron microscopy (SEM). The results showed that when T-f=200 degrees C (iPP was fully molten), the /-CNA cannot encourage -phase crystallization since the nucleation efficiency (NE) of the -NA 3988 was obviously higher than that of the -NA WBG-II. Surprisingly, when T-f was in 179-167 degrees C, an amount of ordered structures survived in the melt, resulting in significant increase of the proportion of -phase (achieving 74.9% at maximum), indicating that the ordered structures of iPP played determining role in -phase crystallization of iPP nucleated with the /-CNA. Further investigation on iPP respectively nucleated with individual 3988 and WBG-II showed that as T-f decreased from 200 degrees C to 167 degrees C, the crystallization peak temperature T-c of iPP/3988 stayed almost constant, while T-c of iPP/WBG-II increased gradually when T-f < 189 degrees C and became higher than that of iPP/3988 when T-f decreased to 179 degrees C and lower, which can be used to explain the influence of ordered structure and /-CNA on iPP crystallization. Using this method, the selection of -NA for /-CNA can be greatly expanded even if the inherent NE of -NA is lower than that of the -NA. (c) 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 41355.