Effect of Barium Loading on CuOx–CeO2 Catalysts: NOx Storage Capacity, NO Oxidation Ability and Soot Oxidation Activity

Fan Lin,Xiaodong Wu,Duan Weng

DOI: https://doi.org/10.1016/j.cattod.2011.03.002

IF: 5.3

2011-01-01

Catalysis Today

Abstract:A series of Ba–Cu–Ce catalysts were prepared by loading different amounts of Ba(Ac)2 on the sol–gel-synthesized CuOx–CeO2 mixed oxides. The activities of the catalysts for soot oxidation were evaluated in 1000ppm NO/10% O2/N2 under loose contact conditions. The catalysts were characterized by XRD, BET, H2-TPR, in situ-DRIFTS and NO-TPO measurements. When Ba loading is between 6 and 10mol.% of Cu+Ce, the catalysts exhibit an onset temperature (Ti) as low as 376°C. NO is oxidized at Cux+ and Cex+ sites and then stored on the adjacent Ba species in form of barium nitrate. Ba(NO3)3 begins to decompose, releasing abundant NO2 at around 370°C under the driving of soot as the reductant. The nitrate-derived NO2 and the NO-derived NO2 initiate the soot combustion over the Ba-modified catalysts with a significantly lowered Ti. The ternary catalysts lose their NOx storage capacity after hydrothermally aged at 800°C for 10h due to the formation of BaCeO3. However, Ba restrains the sintering of (Cu,Ce)Ox, resulting in relatively more favorable redox properties and thus higher activity for NO oxidation. The barium-modified catalysts show lower onset temperatures (470–480°C) of soot oxidation than pure CuCe (509°C) after aging.