Preparation of Cubic Zinc Stannate Nanopowder and Its Application in Silver-Based Electrical Contact Material
Ye Chenlin,Zhang Lingjie,Shen Tao,Mu Chengfa,Yang Hui,Chen Xiao,Fan Xianping
2020-01-01
Rare Metal Materials and Engineering
Abstract:High-purity cubic zinc stannate nanopowder with spinet structure was synthesized by chemical co-precipitation method with different zinc sources, tin sources and precipitants as raw materials. Zinc stannate nanopowders as reinforced phase were applied to strengthen the properties of silver-based electrical contact materials. Ag/Zn2SnO4 electrical contact materials were prepared by mechanical alloying and powder metallurgy technique. The effects of the processing parameters such as heat treating temperature, types of zinc sources and types of precipitants on the microstructure and physical performance of Ag/Zn2SnO4 electrical contact materials were investigated. The morphology and phase of zinc stannate nanopowder were characterized by field emission scanning electron microscopy and X-ray electron diffractometry. The electrical resistivity, hardness and density of Ag/Zn2SnO4 electrical contact materials were also investigated. The results show that using tin chloride, zinc chloride and sodium carbonate as raw materials, under the condition of sintering temperature at 1000 degrees C for 3 h, the optimal electrical resistivity, density and Vickers hardness of the Ag/Zn2SnO4 electrical contact material can reach 2.31 mu Omega.cm, 9.51 g/cm(3) and 656.3 MPa, respectively. Compared with traditional Ag/SnO2 and Ag/ZnO electrical contacts, Ag/Zn2SnO4 electrical contact material has obvious advantages in electrical properties and density. And Ag/Zn2SnO4 electrical contact material also has more compact fracture morphology and shows better interface bonding performance.