Nano Y2-xSiO5:Eux3+: Preparation, Structure Effect on Emitting Properties,Emitting Mechanism
Guang Shan-Yi,Zhang Chao,Xu Hong-Yao,Wang Hai-Yan,Lin Nai-Bo
DOI: https://doi.org/10.3321/j.issn:1001-4861.2007.06.010
2007-01-01
Abstract:Nano-meter Y-2-SiO5:Eu-x, materials were synthesized by sol-gel method, and its structure, and morphology were characterized by XRD, FTIR and TEM. The influence of phase structure, calcination temperature and Eu3+ doping concentration on luminescence properties was investigated. The results show that the materials obtained at calcination temperature below 900 degrees C mainly present non-crystal state, while the materials mainly exhibit crystal state structure when calcined over 900 degrees C. The particle size increased with the calcination temperature. The particle size was 15 similar to 45 nm and 60 similar to 80 nm for amorphous and crystal forms, respectively. The excitation and emission spectra of materials are all affected by phase structure, calcination temperature and Eu3+ doping concentration. For Y2-xSiO5:Eu-x nanocrystal samples, in excitation spectra the charge transfer state (CTS) in crystal state absoption peak appeared red-shifted obviously compared with that in amorphous form, and in emission spectra the strong emission peak corresponding to D-5(0)-> F-7(2) transition was observed and its intensity increased and decreased, respectively, with the calcination temperature for amorphous samples and crystal samples, at the same time two novel sharp emissions peaks were found at longer wavelength and became stronger with particle size. The spectra with respect to the D-5(0)-> F-7(1) transition splitted into sharp triple peaks, but the emission spectra corresponding to D-5(0)-> F-7(0) transition was almost not affected by the crystal phase and the particle size. While in the crystal Y2-x,SiO5:Eu-x of 60 similar to 80 nm, the luminescence intensities of D-5(0)-> F-7(2) and D-5(0)-> F-7(1) transitions were influenced by Eu3+ doping concentration, when the Eu3+ doping concentration was at x=0.4, the luminescence intensity was the strongest.