Corrosion Behavior of X80 Pipeline Steel in Simulated Solution of Ku'erle Soil

XU Cong-min,SHI Kai,ZHOU Yong,ZHANG Rui-feng,LI Xiao,LU Yan-ling,YAO Ting-zhen

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2009.08.015

2009-01-01

Abstract:The electrochemical corrosion behavior and mecha-nism of X80 pipeline steel in simulated solution of Ku' erle soil were investigated bv making use of electrochemical measurement, scan-ning electron microscopic observation, energy dispersive spectrome-tric analysis, and X-ray diffraction analysis. At the same time, the effects of heat treatment and corrosion time on the polarization curves of the pipeline steel were analyzed. Results show that the annealed X80 steel has poorer corrosion resistance than the as-prepared X80 steel, due to the change of microstructure by annealing. Both the as -prepared and annealed X80 steel had similar corrosion tendency. Namely, their corrosion became increasingly severe with extendingtime of corrosion. The as-prepared X80 steel was dominated by in-crease, decrease, and again increase of corrosion rate with extending corrosion time, but the annealed one was dominated by simple in-crease of corrosion rate therewith. The corrosion products are com-posed of Fc(X)H ( surface layer) and Fe3O4(inner layer). The inte-grality and compactness of the corrosion product film had significanteffects on the corrosion behavior and process, and localized corrosion damage of X80 steel. Moreover, the content of C1- in the solution dominated the corrosion severity.