Abstract:M-type barium ferrite with the formula Ba 1− x Sm x Fe 12− y Nb y O 19 ( x = 0.00–0.10, y = 0.00–0.20), which was co-doped with Sm 3+ and Nb 5+ ions, was synthesized experimentally by a modified solid-phase reaction method. The crystal structure of samples was determined by X-ray diffraction, which confirmed that they were of high purity. The X-ray diffraction data were fitted with a full-spectrum correction using GSAS software. By Fourier transform infrared spectroscopy, the samples were observed to exhibit bands due to tetrahedral and octahedral sites at 598 cm −1 and 445 cm −1 , respectively. The samples were examined by field emission scanning electron microscopy, which showed that they partly comprised hexagonal structures but mostly consisted of irregular structures with rounded edges. Characterization of the elemental contents of the samples by energy-dispersive spectroscopy revealed an increase in the contents of Sm and Nb and a decrease in the contents of Ba and Fe. The magnetic properties of the samples were examined using a vibrating sample magnetometer. The results showed that the saturation magnetization and residual magnetization of the samples decreased slightly with an increase in the contents of the dopants. The coercivity reached its maximum value, namely, 3367.53 Oe, when x = 0.04 and y = 0.08.

The Structural and Magnetic Properties of Barium Ferrite Powders Prepared by the Sol-Gel Method

La and Co substituted M-type barium ferrites processed by sol-gel combustion synthesis

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

Synthesis and Characterization of Nd Doped M-type Hexagonal Barium Ferrite Ultrafine Powders

Preparation and Magnetic Properties of Barium Hexaferrite Nanoparticles Produced by the Citrate Process

Synthesis of Barium Ferrite Ultrafine Powders by a Sol–gel Combustion Method Using Glycine Gels

Synthesis and Properties of Barium Ferrite Nano-Powders by Chemical Co-Precipitation Method

Extra up-spin magnetic moments and extraordinary high saturation magnetization of Ni2+ doped barium ferrite in 4f(2) site

Influence of Bi 2O 3 on the structure and magnetic properties of barium ferrite powders materials

Study on magnetic properties of different rare earth doped M-type barium ferrite ultrafine powders

Sintering and Magnetic Characteristics of Barium Hexaferrites with Bi2O3/CuO Additives

Structure and magnetic properties of M-type barium ferrite co-doped with Sm and Nb prepared by solid-phase sintering

Study on the Structural and Magnetic Properties of La-Doped Barium Ferrites

Extra up-spin magnetic moments and extraordinary high saturation magnetization of Ni<sup>2+</sup> doped barium ferrite in 4f<sub>2</sub> site

Preparation of the Percolative Nickel-Zinc Ferrite/Barium Titanate Composite Ceramics with Liquid-Solid Hybrid Method

Improving the Magnetic Properties of Hydrothermally Synthesized Barium Ferrite

Preparation of M-type Barium Ferrite and Characterization of Its Microwave Absorptive Property

Formation of BaFe12-xNixO19 Ceramics with Considerably High Dielectric and Magnetic Property Coexistence

Compositional Control and Millimeter-Wave Properties of Micro-/Nano-Sized $ {M}$ -Type Barium Hexaferrite Synthesized by Hydrothermal Method

An Ultrafine Barium Ferrite Powder of High Coercivity from Water-In-Oil Microemulsion

Influence of La-Co Substitution on the Structure and Magnetic Properties of Low-Temperature Sintered M-type Barium Ferrites