Abstract:A new method for the preparation of nano-zinc oxide was proposed for the effective use of zinc oxide dust (ZOD) containing complex impurities recycled and processed from local plants. Fe2+, Fe3+, Ca2+, Mg2+, Mn2+, Cu2+, and Pb2+, Sn4+, Al3+, Si4+, Bi3+ were selectively extracted from ZOD by alkaline leaching combined with precursor firing process. The effects of thermodynamic analysis of ZOD, Sodium hydroxide(NaOH) concentration(2–8 mol/L), leaching time (15–75 min), autothermal temperature of leaching reaction (43–70 °C), leaching liquid/solid ratio (L/S:5–25 mL/g), and pH were investigated during leaching process. Thermogravimetry-differential thermogravimetry (TG-DTG) analyses were carried out on Zinc carbonate hydroxide (Zn5(CO3)2(OH)6) precursor. In addition, the effects of calcination temperature(400–700 °C) and holding time (1.5–4.0 h) of precursors on average particle size of nano-ZnO were also studied. The results showed the leaching rate of Zn2+ reached 98.35% under the optimum conditions as: NaOH concentration of 6 mol/L, L/S of 20 mL/g, and leaching time of 60 min. Separation rates of Pb2+, Sn4+, Al3+, Si4+ reached 94.63%, 85.08%, 98.03%, 91.48%, respectively at pH = 5.5. Zn5 (CO3)2(OH)6 nano precursors were obtained at pH = 7–8. After the precursor of zinc carbonate was calcined at 400–600 °C for 2 h, high purity (99.53%) nano-zinc oxide was obtained with a particle size of 20 nm, a specific surface area of 23.84 m2/g, a porosity of 32.66%, and a zeta potential of −13.2 mV. This article provides an alternative new idea for the green and comprehensive utilization of industrial ZOD dusts with complex compositions.

Preparation of Zinc Oxide Nano Powder by Microwave Hydrothermal Method and Its Photocatalytic Property

Effect of solution concentration on surface morphology and photocatalytic activity of ZnO thin films synthesized by hydrothermal methods

Preparation of Nano-ZnO with Homogeneous Precipitation and Its Photocatalytic Properity

Liquid-Phase Synthesis of Nano-Zinc Oxide and Its Photocatalytic Property

Controllable microwave and ultrasonic wave combined synthesis of ZnO micro-/nanostructures in HEPES solution and their shape-dependent photocatalytic activities

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Preparation of dispersive zinc oxide nano-particles via hydrothermal modification route

High Speed Shearing: A Novel Approach for High-Quality ZnO Nanoparticle Synthesis and Photocatalytic Activity Control

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

High UV and Sunlight Photocatalytic Performance of Porous ZnO Nanostructures Synthesized by a Facile and Fast Microwave Hydrothermal Method

Hydrothermal Synthesis of Zinc Tungstate Nano-Particles and Investigation on Their Photocatalytic Properties

Biosynthesis Microwave-Assisted of Zinc Oxide Nanoparticles with Ziziphus jujuba Leaves Extract: Characterization and Photocatalytic Application

Preparation, characterization and photocatalytic properties of ZnTiO3 powders

Nanofiber template-induced preparation of ZnO nanocrystal and its application in photocatalysis

Influence of Microwave Hydrothermal Conditions on the Morphology and Particle Size of Zinc Oxide Crystailite

Preparation and characterization of nanocrystalline zinc oxide by a novel solvothermal oxidation route

Preparation of Highly Dispersed and Small-Sized ZnO Nanoparticles in a Membrane Dispersion Microreactor and Their Photocatalytic Degradation

Preparation and Photocatalysis of Nano-Zn/Ce Composite Oxides

Preparation of nano zinc oxide by alkaline treatment of industrial zinc oxide dust

Mn-doped ZnO nanopowders prepared by sol–gel and microwave-assisted sol–gel methods and their photocatalytic properties

Controlled Synthesis Of The Znwo4 Nanostructure And Effects On The Photocatalytic Performance