Abstract:Coiled tubing (CT) is manufactured using plastic processing and weld molding techniques, rendering the weld zone (WZ) susceptible to fatigue fractures under the continuous action of complex alternating loads during field applications. While this risk has garnered significant attention, the underlying mechanisms of its fatigue failure remain elusive. To address this knowledge gap, this study employs an in-situ SEM fatigue test method, coupled with metallographic analysis, hardness testing, SEM observation, and EBSD characterization, to deeply analyze the fatigue microdamage mechanism in the WZ by comparing the fatigue performance of the base material (BM) of the CT with that of WZ. It is found that the microstructure of the BM consists of different scales and shapes of ferrite and a small amount of pearlite nested and intertwined with each other, which has a strong coordinated deformation ability and can effectively relieve stress concentration, delay crack initiation and form a single fatigue source. In contrast, the WZ's ferrite organization is large, uniform, and independent, making it prone to early-stage plastic deformation with weak inter-grain coordination, resulting in the formation of numerous slip bands and multiple crack sources. During the crack propagation stage, the abundant grain boundaries in the BM effectively deflect the crack expansion direction and slow down its progression; while multiple secondary cracks in the weld expand simultaneously and connect with each other, resulting in a higher crack expansion rate than the BM. The research findings provide crucial insights and guidance for enhancing the overall fatigue performance of CT.

INITIATION AND PROPAGATION OF SHORT FATIGUE CRACKS IN A WELD METAL

Orientation Preference and Fractal Character of Short Fatigue Cracks in a Weld Metal

In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant

A Novel Method for Characterizing the Fatigue Crack Propagation of Steel Via the Weak Magnetic Effect

Very High Cycle Fatigue Behavior And Life Prediction Of A Low Strength Weld Metal At Moderate Temperature

Strain Visualization of Growing Short Fatigue Cracks in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint: Intergranular Cracking and Crack Closure

Quantitative Relationship Between Weld Defect Characteristic and Fatigue Crack Initiation Life for High-Cycle Fatigue Property

Initiation Behavior of Microscopic Short Cracks in Weld Toe of Structural Steel Q345B

Experimental Investigation of Fatigue Behaviour for Welded Joint with Mechanical Heterogeneity

Fatigue Crack Growth Behavior of the MIG Welded Joint of 06Cr19Ni10 Stainless Steel

Fatigue crack initiation behaviors around defects induced by welding thermal cycle in superalloy IN617B

Initiation and propagation mechanism of fatigue crack in ultra-thick titanium alloy vacuum electron beam welding joint

Initiation and Propagation of Fretting Fatigue Crack in the Very Long Fatigue Life.

Numerical simulation of distortion-induced fatigue crack growth using extended finite element method

INITIATION AND PROPAGATION OF FATIGUE CRACK INEDGE REGION OF HOLE IN A SHEET WITH CENTRAL HOLE

An Experimental Methodology for Quantitative Characterization of Multi-Site Fatigue Crack Nucleation in High-Strength Al Alloys

Mechanisms Affecting the Difference in Fatigue Resistance Between Welds and Base Materials Were Investigated Based on In-Situ Fatigue Method

Initiation of internal fatigue crack in a carbide-free bainitic steel during high cycle fatigue

Fatigue Crack Initiation for Al-Zn-Mg Alloy Welded Joint

The Fatigue Crack Initiation Life of X60 Pipeline Steel after Pre-tension Deformation

MORPHOLOGICAL EVOLUTION OF INTERNAL FATIGUE MICROCRACKS IN Α-Iron DURING DIFFUSIVE HEALING