Abstract:Purpose At present, the conventional method of preparing cationic fluorinated acrylic latex is to emulsify copolymerised monomers with cationic surfactants. However, there has been a wide concern about using Gemini surfactants to prepare cationic polymer latex to improve its properties. The purpose of this paper was to focus on the synthesis of novel self-crosslinked cationic fluorinated acrylic latex (SCFAL), during which the copolymerised monomers were initiated with a water soluble azo initiator and emulsified with mixed surfactants of Gemini emulsifier and alkyl polyglycoside (APG). Design/methodology/approach The novel SCFAL was prepared successfully by the semi-continuous seeded emulsion polymerisation of butyl acrylate, methyl methacrylate, hexafluorobutyl methacrylate (HFMA) and hydroxy propyl methacrylate (HPMA) in aqueous medium. Findings The conversion is the maximum and the coagulation percentage the minimum when the amounts of emulsifier and initiator are 8 and 0.6 per cent, respectively. The average particle size of the latex is significantly reduced with the increase of the amount of emulsifiers used. However, the average particle size of the latex is increased with the increase of the amount of HPMA. The particle size of the latex is of a unimodal distribution, which means that the particle size was reasonably uniform. Contact angle is increased with the increase of the amount of the HFMA. Practical implications The novel SCFAL can be widely used as significant components in the field of coatings, leather, textile, paper, adhesives and so on. Originality/value SCFAL, which was emulsified with novel mixed surfactants of Gemini surfactant and APG, has been prepared successfully. Influences of amount of initiator, emulsifier, HPMA and HFMA on emulsion polymerisation and/or properties of novel latex are investigated in detail.

Synthesis, Modification and Characterization of Core–shell Fluoroacrylate Copolymer Latexes

Synthesis and Redispersibility of Poly(styrene-block-n-butyl Acrylate) Core–Shell Latexes by Emulsion Polymerization with RAFT Agent–Surfactant Design

Synthesis and characterization of core-shell acrylate based latex and study of its reactive blends

Fabrication of core-shell polyacrylate latex pressure sensitive adhesives modified by fluorinated monomer and film properties

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Preparation and characterization of fluorocarbon latex modified by diallyl malate

SYNTHESIS, CHARACTERIZATION AND CROSSLINKING REACTION OF REACTIVE COMPOSITE LATEX

Synthesis and Properties of Novel Fluorinated Cationic Polymer Latex

Study on preparing novel cross-linked and fluorinated acrylate latex

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

Synthesis and Properties of Novel Self-Crosslinked Cationic Fluorinated Acrylic Latex Prepared with Novel Emulsified System

Synthesis and characterization of fluorinated polyacrylate latex emulsified with novel surfactants

Preparation and Structure Control of Hollow Polymer Particles——Synthesis and Effect on the Hollow Structure of the Core Latex

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Synthesis and characterization of fluoro-silicone polyacrylate latex emulsified with novel green surfactants

Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer

Preparation of Polyacrylate - Polysiloxane Core - Shell Latex Particles

Synthesis and Performance of A Self Crosslinkable Acrylate Copolymer with High Compatibility for an Oil Well Cement Modifier

Research of the Synthesis and Film Performance of Silica/poly(st-Ba-mps) Core-Shell Latexes Obtained by Miniemulsion Co-Polymerization

Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO₂ and Fluorine

Synthesis and Film Performances of SiO2/P(MMA-BA) Core–shell Structural Latex