HYPERBRANCHED AZO POLYMERS SYNTHESIZED BY AZO-COUPLING REACTION OF A_2/B_3 MONOMERS
He Yaning,Li Yujing,Yin Jianjun,Wang Xiaogong
DOI: https://doi.org/10.3321/j.issn:1000-3304.2008.02.015
2008-01-01
Acta Polymerica Sinica
Abstract:An A_2+B_3 method of preparing hyperbranched azo polymers by azo-coupling reactions was described.The hyperbranched precursor with diazonium salt groups on the periphery was prepared by step-growth polymerization of A_2(diazonium salts of 4,4′-diamino diphenyl sulphone)/B_3(benzene-1,3,5-tricarboxylic acid tri-2-(N-ethylanilino)ethyl ester)monomers through azo-coupling reaction.Benzene-1,3,5-tricarboxylic acid tri-2-(N-ethylanilino)ethyl ester was prepared by Schotten-Baumann reactions between 1,3,5-benzenetricarbonyl chloride and N-ethyl-N-hydroxyethyl-aniline.Then the hyperbranched precursor with diazonium salt groups on the periphery was further reacted with N,N-diethyl aniline by azo-coupling reaction to obtain the final hyperbranched azo polymer.The azo polymer was characterized by the spectroscopic methods and thermal analysis.The phase transition behavior of the hyperbranched azo polymer was studied by using the differential scanning calorimetry (DSC).The hyperbranched polymer showed a second-order phase transition of typical amorphous substances.The T_g of the hyperbranched azo polymer was about 161℃.As containing the donor-acceptor type azo chromophores,the polymer showed typical spectral characteristics of the pseudo-stilbene type azo chromophores.The λ_ max value of the hyperbranched azo polymer,corresponding to the π-π transition,was about 465 nm.Spin-coated thin films of the hyperbranched azo polymer were used to carry out the SGR inscription experiments.Two p-polarized Ar~+ laser beams (488 nm) with an intensity 80 mW/cm~2 were used to produce the interference pattern on the polymer film.After irradiated for 1000 s at room temperature,the surface modulation depth was about 100 nm,and the grating spacing was about 730 nm.The modulation depth depended on the irradiation energy,and the spatial period depended on both the angle between the two interfering beams and the wavelength of the writing beams.Complex patterns could be inscribed when two gratings were recorded orthogonally to each other at the same location.