Recrystallization Behavior of a Multiscalar Microlaminate

Shi Guodong,Wang Zhi,Liang Jun,Wu Zhanjun,Chen Guiqing

2011-01-01

Rare Metal Materials and Engineering

Abstract:A multiscalar microlaminate, NiCoCrAl/ZrO2-8Y(2)O(3) was annealed in vacuum at 1050 degrees C for 0.5, 2 and 4 h, respectively. The microlaminate comprised metal/ceramic thin stacks and tough phase layers with thickness ranging from 5 mu m to 25 mu m. After annealing, the variation in microstructure of metal layers of the microlaminate depended on their layer-thicknesses. The metal-layers with layer-thicknesses more than 20 mu m was more difficult to be recrystallized than those with layer-thicknesses less than 13 mu m. And when the thicknesses of the metal layers were less than 13 mu m, recrystallized grain sizes increased with the increasing layer-thickness. Furthermore, the mechanism of recrystallization for the metal-layers with different thicknesses was discussed.