Preparation and Characterization of N-Doped TiO_2 Nanotube

Zhang Liyuan,Cao Yang,Liu Zhongxin,Yu Xiaolong,Lü Zuofeng

DOI: https://doi.org/10.3969/j.issn.0258-7076.2011.04.006

2011-01-01

Abstract:TiO2 nanotube arrays were prepared on the surface of pure titanium sheet by anodic oxidation method.N was doped using NH3,which engendered by the volatilization of NH3·H2O during annealing.The characteristics of TiO2 nanotube were investigated by FESEM,XRD,XPS,UV-vis.The results indicated that the diameter of undoped,N-doped TiO2 nanotube was 70~80 nm,the thickness of the wall was 5~10 nm,the length of the tube was 400~500 nm.N was successfully doped into crystal lattice and the content of N was 0.68%(atom fraction).Undoped TiO2,N-doped TiO2 annealed at 400 ℃ was entirely anatase or anatase mixed with rutile.N-doped TiO2 exhibited stronger absorption under the visible light compared with undoped TiO2.Methyl orange was used as the degraded agent in photocatalytic experiment,the effect of N-doping,initial concentration of Methyl orange and pH on photocatalytic property were studied by spectrophotometer.The results showed that the degradation of methyl orange coincided with first order kinetics,the photocatalytic property of N-doped TiO2 nanotube arrays film was 11.1 % higher than undoped TiO2 nanotube arrays film after exposed for 150 min.The optimum concentration of methyl orange was 20 mg·L-1.The optimum pH value was 1.