Corrosion inhibition performance of composite based on chitosan derivative
Yuxuan Zheng,Yuhua Gao,Haihua Li,Meifang Yan,Ruhui Guo,Zhenfa Liu
DOI: https://doi.org/10.1016/j.molliq.2020.114679
IF: 6
2021-01-01
Journal of Molecular Liquids
Abstract:The shortage of water resources has resulted in municipal wastewater(MWW) becoming the main source of industrial cooling water replenishment. However, MWW causes severe erosion in carbon steel water pipelines, and the most widely used phosphorus-containing corrosion inhibitor currently available, 2-hydroxyphosphonocarboxylic acid (HPAA), only shows effective inhibitory effects at high doses. In this work, a natural polymer, N-carboxylated chitosan (NCC), was developed via a pollution-free method, and the resulting compound was formulated as a water treatment corrosion inhibitor. This compound was composited with NCC, HPAA, gluconic acid sodium (GA), and ZnSO4, and the resulting compound was abbreviated as NHGZ. This process greatly reduced the use of phosphorus-containing compounds. The performances of NCC and NHGZ were then evaluated by electrochemical and weight-loss studies. Electrochemical test results demonstrated that NCC is a cathodic corrosion inhibitor, whereas NHGZ is a mixed corrosion inhibitor. The weight-loss studies showed that the corrosion rate of NHGZ in MWW at 40 degrees C was only 0.0254 mm/y, which was lower than that of the uninhibited sample of 0.9268 mm/y. This effect was attributed to the ability of the NHGZ to molecularly adsorb onto and form a stable protective inhibitor film on the surface of carbon steel. Scanning electron microscopy, energy-dispersive X-ray spectroscopy, atomic force microscopy, X-ray photoelectron spectroscopy, and theoretical adsorption simulations were employed to explain the possible corrosion inhibition mechanism of NHGZ. (C) 2020 Elsevier B.V. All rights reserved.