EFFECT OF SINTERING TEMPERATURE ON MECHANICAL PROPERTIES OF MACHINABLE 3Y-TZP BLANKS FOR DENTAL ALL-CERAMIC SUBSTRUCTURES

Yang Sefei,Yang Liqiang,Jin Zhihao
DOI: https://doi.org/10.3969/j.issn.1006-2874.2006.06.001
2006-01-01
Abstract:3Y-TZP starting powder (0.3μm in particle size on average)was prepared by 200MPa isostatic-hydraulic press and pre-sintered at different temperatures (800℃, 900℃, 1000℃and 1100℃). Then the pre-sintered blanks were sintered at 1500℃, 1550℃, and 1600℃. Mechanical properties and machinability were investigated. SEM was used to observe the fracture surface of the samples. Results showed that machinability of pre-sintered blanks was best at 900℃and the relative density was 50% higher. The fracture toughness of sintered samples was 14 MPa·m1/2 at 1550℃. Three-point flexural strength of sintered samples had no statistically significant difference at 1550℃from that at 1600℃(P>0.05).