High-silica FAU zeolite through controllable modulation framework strategy for VOCs adsorption under high humidity
Qiang Yu,Wenna Zhang,Junjie Li,Wen Liu,Yanan Wang,Weifeng Chu,Xinbao Zhang,Longya Xu,Xiangxue Zhu,Xiujie Li
DOI: https://doi.org/10.1016/j.micromeso.2023.112570
IF: 5.876
2023-03-29
Microporous and Mesoporous Materials
Abstract:Although FAU zeolites have been widely used as absorbents for volatile organic compounds (VOCs) removal, preparation of high-silica FAU zeolite to expand its application under high humidity is still a big challenge. Here, two high-silica FAU zeolites were successfully prepared through the controllable modulation framework strategy. By carefully matching the degrees of dealumination and Si-insertion, the zeolite (FAU-H) with an ultra-high SiO 2 /Al 2 O 3 ratio of 957 was obtained. FAU-H exhibited similar high adsorption capacities of VOCs (e.g. m-xylene and toluene) under dry and humid conditions, more importantly, its adsorption capacity of m-xylene was 25% higher than the industrial high-silica FAU zeolite (HSZ-390HUA) from Tosoh Corporation. When the dealumination degree was mismatched with that of Si-insertion, imperfect FAU-M (SiO 2 /Al 2 O 3 = 108) with the existence of some defect sites was obtained that becomes a good candidate for the adsorption removal of small VOCs molecules (e.g. isopropanol). The moderate interaction between VOCs and zeolite framework is proved a key factor for small molecules adsorption on basis of the DFT calculations. Moreover, the fitted kinetic models, desorption tests, and adsorption−desorption cycling tests proved the good regenerability of FAU-H and FAU-M. Therefore, the proposed high-silica FAU zeolites are promising adsorbents for VOCs removal.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied