Abstract:In this paper, the fatigue life of 2D woven ceramic-matrix composites, i.e., SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate, at room and elevated temperatures has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. The Budiansky-Hutchinson-Evans shear-lag model was used to describe the microstress field of the damaged composite considering fibers failure. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. The interface shear stress and fibers strength degradation model and oxidation region propagation model have been adopted to analyze the fatigue and oxidation effects on fatigue life of the composite, which is controlled by interface frictional slip and diffusion of oxygen gas through matrix multicrackings. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface/fiber oxidation model, interface wear model and fibers statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfy the Global Load Sharing (GLS) criterion. When the broken fibers fraction approaches to the critical value, the composites fatigue fractures. The fatigue life S-N curves of 2D SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate composites at room temperature and 800, 1000 and 1200 °C in air and steam have been predicted.

The Predictions and Applications of Fatigue Lifetime in Alumina and Zirconia Ceramics

Prediction of Fatigue Lifetime in Bio-Ceramics

Fatigue Fracture Behavior of Zirconia Ceramic in Water Environment

In Vitro Cyclic Fatigue and Hydrothermal Aging Lifetime Assessment of Yttria-Stabilized Zirconia Dental Ceramics

Strength Degradation and Lifetime Prediction of Dental Zirconia Ceramics under Cyclic Normal Loading.

A Comparison of Failure Predictions by Dynamic Bending and Cyclic Bending Fatigue Techniques for Y2O3ZrO2 Ceramics

BEHAVIOR OF CRACK PROPAGATION IN SOME BIO-CERAMICS

Plastic Energy Dissipation Model for Lifetime Prediction of Zirconium and Zircaloy-4 Fatigued at RT and 400°C

Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

Fatigue Damage Modes of Bilayered Zirconia and Alumina Dental Composites

Research On The Cyclic Fatigue Behavior Of Zirconia Ceramics At The Room Temperature

Lifetime prediction of time-dependent thermomechanical fatigue of high temperature alloys

A fatigue life prediction approach for porosity defect-induced failures in directed energy deposited Ti-6Al-4V considering crack growth environment

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

In-phase Thermomechanical Fatigue Lifetime Prediction of Nickel-Based Single Crystal Superalloys from Smooth Specimens to Notched Specimens Based on Coupling Damage on Critical Plane

Low Cycle Fatigue Behavior and Deformation Mechanisms of Zirconium and Zircaloy-4

Mechanical and Environmental Factors in the Cyclic and Static Fatigue of A Machinable Glass-Ceramic

Micromechanical life prediction method of fiber-reinforced ceramic-matrix composites subjected to stochastic overloading at room temperature

Thermal Fatigue Life Prediction of Ni Base Alloy Ceramic Composite Coating

Fatigue Reliability of Dental Ceramic Materials – an in Vitro Study

The Effects of Load and Frequency on the Fatigue Damage of Bi-Layered Zirconia and Alumina Dental Composites